Refractory material for iron-making system
Product Description
1、Shaped refractory material for iron-making system
Silicate series alumina shaped product for hot blast stove
AL2O3% Refracto-riness
℃ Apparent porosity
% Cold compressive strength Reheat-ing
linear change Initial softening point under load 0.2MPa×50h
Creep rate not more than
Fire clay bricks for hot blast heater RN-42 ≥42 ﹥1760 ≤24 ≥30 1450℃×2h
0~-0.4 ≥1400
RN-40 ≥40 ﹥1740 ≤24 ≥25 1350℃×2h
0~-0.3 ≥1350
RN-36 ≥36 ﹥1700 ≤26 ≥25 1350℃×2h
0~-0.5 ≥1300
High alumina bricks for hot blast heater RL-65 ≥65 ﹥1790 ≤22(24) ≥50 1500℃×2h
0~-0.4 ≥1500
RL-55 ≥55 ﹥1770 ≤22(24) ≥45 1500℃×2h
0~-0.4 ≥1470
RL-48 ≥48 ﹥1750 ≤22(24) ≥40 1450℃×2h
0~-0.4 ≥1420
Low creep fire day bricks for hot balst heater DRN-130 ≥48 ﹥1760 ≤20(23) ≥60 1400℃×2h
±0.2 ≥1520 1300℃
≤0.8
DRN-125 ≥45 ﹥1750 ≤20(23) ≥60 1400℃×2h
±0.2 ≥1500 1250℃
≤0.8
Low creep high alumina bricks for hot blast heater DRL-135 ≥65 ﹥1790 ≤20(23) ≥70 1450℃×2h
0~-0.4 ≥1550 1350℃
≤0.8
DRL-140 ≥65 ﹥1790 ≤19(23) ≥75 1450℃×2h
0.2~0.1 ≥1600 1400℃
≤0.8
DRL-145 ≥70 ﹥1790 ≤19(23) ≥80 1500℃×2h
0.2~0.1 ≥1650 1450℃
≤0.8
DRL-150 ≥75 ﹥1790 ≤18(23) ≥85 1500℃×2h
0.2~0.1 ≥1700 1500℃
≤0.8
Refractory ball for hot blast stove
AL2O3% Fe2O3% Apparent ponosity Refract-oriness Bulk density
g/cm3 Cold compressive strength Reheating linear change Initial softening point under load
Fireclay ≥48 ≤2.0 ≤23 >1790 ≥2.1 ≥10000 -0.4~-0.2 ≥1400
High-strength high-
Alumina ≥65 ≤1.5 ≤23 >1790 ≥2.2 ≥12000 -0.4~-0.1 ≥1480
Mullite ≥75 ≤1.0 ≤22 >1790 ≥2.4 ≥19000 0.1~0.2 ≥1550
High-intensive high-
Density high-alumina ≥75 ≤1.5 ≤23 >1790 ≥2.55 ≥20000 0.1~0.3 ≥1480
Low creep high-alumina 65# ≥65 ≤1.5 ≤22 >1790 ≥2.60 ≥12000 0.1~0.2 ≥1490
75# ≥75 ≤1.5 ≤21 >1790 ≥2.65 ≥15000 0.1~0.2 ≥1500
80# ≥80 ≤1.0 ≤20 >1790 ≥2.65 ≥15000 0.1~0.2 ≥1520
Alumel-zirconium LZ-5 ≥65 ZrO2≥5 ≤22 >1790 ≥2.60 ≥14000 0.1~0.3 ≥1500
LZ-8 ≥70 ZrO2≥8 ≤22 >1790 ≥2.65 ≥15000 0.1~0.3 ≥1520
Silicon SiO2≥95 ≤23 >1790 ≥2.4 ≥12000 1000℃ thermal expansion porosity ≤0.9%
1500℃thermal expansion porosity ≤1.2%
Aluminum silicate series of shaped product for blast furnace
AL2O3% Fe2O3% Refractor-
iness
℃ Apparent psnosity
% MPa cold compressive strength 1450℃×2h
Reheating linear change % 0.2MPa the start refractoriness under load
Phosphoric acid dipped clay brick ≥45 ≤1.8 - ≤14 ≥60 -0.2~0 ≥1450
Notes:the element of P2O5 is more than 7%
Clay brick for blast furnace ZGN-42 ≥42 ≤1.6 >1760 ≤15 ≥60 0~0.2 ≥1450
GN-42 ≥042 ≤1.7 >1760 ≤16 ≥50 0~0.3 ≥1430
High-alumina for blast furnace GL-65 ≥65 ≤2.0 >1790 ≤19 ≥60 1500℃×2h
0~0.2 ≥1500
GL-55 ≥55 ≤2.0 >1780 ≤19 ≥50 1500℃×2h
0~0.2 ≥1480
GL-48 ≥48 ≤2.0 >1760 ≤18 ≥50 1450℃×2h
0~0.2 ≥1450
Send Inquiry to this Member
Related Products of this Company
This member assumes full responsibility for the content of this listing. DIYTrade accepts no responsibility whatsoever in respect of such content.
To report fraudulent or illegal content, please
click here.
China Suppliers Quick Searching:
,