Standard specification for wrought Iron-Cobalt high magnetic saturation Alloy(UNS K92650
Sheet Thickness:0.1mm~5.0mm
Plate Thickness:3.5mm~40.0mm
Bar Dia 8.0mm~Dia150.0mm
Products Application
Aviation and aerospace components,The motor rotor, magnet pole head, relays, transducers, Magnetic shaft ,etc
Description
Hiperco27 is a new kind of soft magnetic alloy and also called FeCo27. while its permeability and the coercive force slightly smaller than hiperco50, but the mechanical toughness and ductility is better, can be competent for machining, the saturated magnetic induction intensity and Curie temperature are fairly to HiperCo50 .
Parameter
TABLE 1 Chemical Requirement
Element Composition,%
C ≤ 0.025
Mn≤ 0.35
SI≤ 0.35
P≤ 0.015
S≤ 0.015
CR≤ 0.75
NI≤ 0.75
CO 26.50-28.50
V≤ 0.35
FE remainder
TABLE 2 Physical Requirement
Property Target
Density,g/m³ (kg/m³ ) 7.95(7950)
Electrical resistivity,μΩ-cm (μΩ-mm) 19(190)
Curie temperature °C 925
saturation magnetostriction,10-6 36
Modulus of elasticity psi (GPa) 23.6(2.36)
Thermal conductivity,cal/cm.s. °C(W/m.k) 24x10/6(166)
Thermal expansivity,10-/6°C 0.131(54.8)
TABLE 3 Dc Magnetic property requirements
Minimum Magnetic Flux Density KG,(T)
for magetic field strengths of
50Oe 100Oe 50Oe 200Oe
Product Form Size 4KA/m 8A/m 12KA/m 16KA/m
Cold rolling strip All 18.7(1.87) 20.3(2.03) 21.2(2.12) 21.7(2.17)
Bar up to 0.250 in (6.35mm) 18.7(1.87) 20.3(2.03) 21.2(2.12) 21.7(2.17)
Bar Over 0.250 in (6.35mm) 11.0(1.1) 17.5(1.75) 19.5(1.95) 21.0(2.10)
Forging Billet,Hot rolled Plate, All 11.0(1.1) 17.5(1.75) 19.5(1.95) 21.0(2.10)
Tot Rolling Strip
TABLE 4 Typical DC magnetic Properties
Product Form Strip Round Bar
Product Size,in (mm) 0.014(0.35) 0.500(12.7)
Heat Treatment temperature,°C 845 925
Magnetic Field Strength,Oe(A/m) Flux Density,KG (T)
2(160) 5.0(0.25 ................
5(400) ................ ................
10(800) 13.5(1.35) 11.0(1.10)
20(1600) 17.0(1.70) 14.0(1.40)
50(4000) 19.2(1.92) 18.5(1.85)
75(6000) 21.0(2.10) 19.5(1.95)
100(8000) 21.5(2.15) 20.5(2.05)
Corcive Field Strength,Oe(A/m) 1.7(140) 3.0.0(240)
Residual Induction,KG (T) 8.5(0.85) 6.0.0(0.60)
Coercive Field Strength and Residual measured from a maximum magnetic field strength of 100 Oe (8000 A/m)
TABLE 5 Typical 400 Hz ac Core Losses for strip
Heat treatment Strip Core Loss,W/Ib (W/Kg) at Specified
Temperature,°C Thickness, Maximum Flux Density
in,(mm) 10KG(1.0T) 15KG(1.5T) 20KG(2.0T)
845 0.014(0.36) 17(37) 35(77) 65(140)
845 0.010(0.25) 13(29) 25(55) 50(110)
750 0.014(0.36) 18(40) 37(82) 68(150)
750 0.010(0.25) 15(33) 27(60) 55(120)
TABLE 6 Typical Mechanical Properties
0.2% Yield Ultimate Tensile %Elongation
Condition stress Strength in 2 in
Ksi MPa KSI MPa (50mm)
Cold rolling Strip 165 1140 167 1150 7
Strip annealed at 845 °C 41 280 80 550 12
Strip annealed at 750 °C 50 340 90 625 15
WHY US?
1.Specialized in manufacturing high-precision alloy for 23+ years
2.We can tailoring your unique requirements with ASTM, UNS ,GOST, standard
3. Good quality control in production process, ISO9001:2008, SGS, CQC, approved.
4. The whole process from raw material to finished products can be traced.
5. 40000 square meters workshop, advanced facilities and test equipment .