| D555Matting Agent | ||||||||
| Characteristic:Reduce the brightness of the paint film、Good matting ability with smooth | ||||||||
| Match with | 2K solid color/Clear Coat series | |||||||
| Surstrates Treatment | Using tack rag to clear sanded surstrates | |||||||
| Blending Ratio | Name | 2K Solid Color/Clear Coat | D555 Matting Agent | |||||
| All matte | 100 Parts | 100 Parts | ||||||
| Half matte | 100 Parts | 50 Parts | ||||||
| Mixing Ratio | Temperature | Name | Blended Matting Solid Color | Hardener Seires | Thinner Series | |||
| According to the Hardener and Thinner to choose temperature | Weight Ratio | 100 Parts | 50 Parts | 15-20 Parts | ||||
| Volume
Ratio |
2 Parts | 1 Part | 0.2-0.5 Parts | |||||
| Remarks | Adding Thinner immoderately will effect Matting effects | |||||||
| Pot Life | 30 Minutes at 25℃ after blended | |||||||
| Spray viscosity | 17-20 Seconds at 25℃ | |||||||
| No.of Coats | 2-3 Coats | |||||||
| Flash-off Time | 3-5 Minutes | |||||||
| Each thickness | 30-40 Micron | |||||||
| Spray Pressure | Gravity Feed: 1.3-1.5/3-4.5kg
Siphon Feed: 1.8/3.5-5kg |
|||||||
| Drying Time | Temperature | Dust Free | Dry to Handle | Thorough Dry | ||||
| 250C | 10 Minutes | 4 Hours | 6 Hours | |||||
| 600C | 5 Minutes | 40 Minutes | 40 Minutes | |||||
| Sandability and Polishabiility | No sanded | |||||||
| Shelf Life | 1 year in original sealed (can continue to use after passing inspection ) | |||||||
| Packaging | 4L | |||||||
| The above products are designed for special using, please reference to the label and detailed security parameter , the product users should comply with the health and safe treatment regulations | ||||||||
| The above technical data is correct, but we don't provides guarantee, because the final result will be effected by the environment and the use of methods. | ||||||||