| D-1060 Epoxy Primer | ||||||||
| Characteristic:two pack epoxy primer with strong chemical corrosion resisting ability and adhesion,and also have good leveling and gloss performance | ||||||||
| Surstrates | Steel、glass steel and hardened original paint surstrates | |||||||
| Surstrates Treatment | Remove sanded contaminations with degreaser | |||||||
| Mixing Ratio | Temperature |
Name | D-1060 Epoxy Primer | D-1160 Epoxy Primer Hardener | 2K Series Thinner | |||
According to choose mixing thinner to apply to temperature |
Weight Ratio | 100 Parts | 25Parts | 25Parts | ||||
| Volume Ratio | 10 Parts | 1 Part | 1 Part | |||||
| Pot Life | 4hours at 250C | |||||||
| Spray viscosity | 20-22 Seconds at /200C | |||||||
| No.of Coats | 2-3coats | |||||||
| Flash-off Time | 5-10 Minutes at 250C | |||||||
| Each thickness | 25-30 Micron | |||||||
Spray Pressure |
Gravity Feed: 1.8/3-4.5kg
Siphon Feed: 1.8/3.5-5kg |
|||||||
| Drying Time | Temperature | Dust Free | Dry to Handle | Thorough Dry | ||||
| 250C | 30 Minutes | 4 Hours | 6 Hours | |||||
| 600C | 15 Minutes | 40 Minutes | 40 Minutes | |||||
| Sandability and Polishabiility | Wet sanding with P80-P100, or dry sanding with P360-P400 | |||||||
| Shelf Life | D1060 Epoxy primer:2 years in original sealed,D1160 Epoxy primer hardener:1 years in original sealed (can continue to use after passing inspection ) | |||||||
| Packaging | D1060 Epoxy primer: 4L; D1160 Epoxy primer hardener:400g | |||||||
| The above products are designed for special using, please reference to the label and detailed security parameter , the product users should comply with the health and safe treatment regulations | ||||||||
| The above technical data is correct, but we don't provides guarantee, because the final result will be effected by the environment and the use of methods. | ||||||||