| Model: | H-133 |
|---|---|
| Brand: | KNG |
| Origin: | Made In China |
| Category: | Chemicals / Adhesives & Sealants |
| Label: | polyurethane sealant , pu adhesive , pu sealing |
| Price: |
-
|
| Min. Order: | 2000 pc |
| Live Chat: | Last Online:16 May, 2012 |
Description:
H-133 PU automobile glass sealant is a single component polyurethane sealants of high modulus, moisture curing, weatherproof, waterproof, low temperature resistant and anti-aging properties. It can be used for assemble and reparation of windshield glass, back window glass and side window glass for automobiles. and can be directly used for the high strength adhesion of the glass and the body of the automobile.
Application:
1. Sealing of automobile parts, railway, containers and ship (as bonding, caulking, door and window seals, floorboard gap and so on waterproofing).
2. Apply to metal containers, Air conditioning, plastic products and board Seals.
3. Polyurethane Sealant Application:
4. The sealed place must be completely cleaned and dried. If necessary, washing them with solvents such as toluene or acetone.
5. In order to keep better appear range. The joint of cover outside areas should be masked with tape before sealants apply.
6. Sealant can be repaired immediately and the masking tape should be removed before the
sealant skins.
7. Previous using experiment is necessary beforehand.
Characteristics:
1. Single Component, Moisture-solidifying, and No Dripping for Vertical Plane Construction;
2. Fast Solidification; Elastic, Good Initial Adhesion, High Strength;
3. Outstanding Application Property;
4. High Dynamic Load Enduring Ability;
5. Good Adhesion with Various Base Materials Such As Glass, Aluminum Plate etc.;
6. Short Drawing Wires When Gluing Stops;
7. No Corrosion on Base Material, No Penetration Pollution;
8. Good Aging Resistance and Weather Resistance Property;
9. Excellent adhesion for most building materials including glass, ceramic, aluminum, plastic.
10.Excellent contact-change ability, no seasonal limited use.
Technical Data:
|
Item |
Properties |
|
Appearance |
Black paste |
|
Surface drying time |
20-60 |
|
Curing rate(mm/24) |
3-5 |
|
Destiny(g/ml) |
1.3±0.1 |
|
Volatile component(≤,%) |
4 |
|
Hardness (shore A) |
45-60 |
|
Slack(≤,mm) |
0 |
|
Tensile strength(≥,Mpa) |
4 |
|
Extension at break (≥,%) |
500 |
|
Shear strength(≥,Mpa) |
3 |
|
Fracture strength(≥,N/mm) |
15 |
|
Strength at a given elongation(≥,MPa) |
1.2 |
|
Operating temperature( oC ) |
-45~90 |
Instruction:
The sealed place must be completely cleaned and dried. If necessary, washing them withsolvents such as toluene or acetone.
In order to keep better appear range. The joint of cover outside areas should be masked with tape before sealants apply.
Sealant can be repaired immediately and the masking tape should be removed before the sealant skins.
Previous using experiment is necessary beforehand.
Limitations:
1. Don't use in structure glazing.
2. Don't use in aquarium assembly and sealing.
3. Don't use in places where have permeated grease, plasticizer or solvent such as wood permeated oil, uncured or half-cured resins. etc.
4. Don't use in mobility over connect joints.
5. Don't use to joints which is hidden in earth or immersed in water for long time.
6. Don't use to complete sealing space, results to lack of hydrosphere, can't good solidify
Packing:
310ml aluminum tube packing
400ml 600ml flexible packing