| Model: | NT2000G |
|---|---|
| Brand: | NAR |
| Origin: | Made In China |
| Category: | Services / Advertisement & CI / Advertising Material |
| Label: | Self Adhesive Vinyl , SAV , Self Adhesive Film |
| Price: |
US $2
/ qm
|
| Min. Order: | 1000 qm |
| Live Chat: | Last Online:08 May, 2012 |
Technical Data Sheet
NAR® NT2000G
White Glossy Calendered PVC Vinyl
Features:
l Soft and seamless vinyl, specially for solvent printers
l Good sheet stability and lay flatness
l Excellent printability, conversion and application characteristics
l High gloss for superior appearance
l High cost performance for short term promotional graphics
l Excellent adhesion to a wide variety of substrates
Description
Film: 100 micron glossy white, soft monomeric calendered PVC film
Adhesive: Permanent clear solvent acrylic adhesive
Backing: One side PE and silicon coated wood pulp paper, 140gsm
Width: 0.914/1.06/1.27/1.37/1.52m
Length: 50/100/250m
Shelf Life: Up to 1 year at 20℃ and relative humidity of 50%
Durability: Up to 1 year
Suit for: Common Applications
Solvent inkjet Eco solvent inkjet • Vehicle graphics
Cutting Cold over laminating • Glass wall advertising
UV curable Water based inkjet • Curve advertising
Screen printing Die Sublimation • Durable Signs and Labels
• Exhibition graphics
Physical Characters
|
Properties |
units |
Test method |
Average value |
|
Thickness - film |
µm |
GB/T6672-2001 |
100±5 |
|
Weight- finished product Gloss 60° Initial Adhesion 180°Peel strength(steel,24h) |
g/m² % N/inch N/inch |
GB4669-1995 GB8807-88 FINAT9 FINAT1 |
290±20 70min 6min 11min |
|
Dimensional stability MD |
% |
FINAT14 |
0.8max |
|
Dimensional stability CD |
% |
FINAT14 |
0.5max |
|
Elongation at break MD |
% |
GB/T1040.1-2006 |
140~260 |
|
Elongation at break CD |
% |
GB/T1040.1-2006 |
120~280 |
|
Tensile Strength at break MD |
N/25 mm |
GB/T1040.1-2006 |
50~90 |
|
Tensile Strength at Break CD Minimum application temperature Temperature range |
N/25 mm °C °C |
GB/T1040.1-2006 |
40~85 + 10 -20 ~ +70 |
ü Information on physical characteristics is based upon tests we believe to be reliable. The values listed herein are average, minimum or maximum values. They are intended only as a source of information and are given without guarantee and do not constitute a warranty. Purchasers should independently determine, prior to use, the suitability of any material for their specific use.
ü All technical data is subject to change without prior notice.
ü In order to avoid loss of quality, the NAR product should be stored in suitable conditions, at temperature around 20℃ and relative humidity of 50%. Under this condition, NAR product can be stored for period of 1 year. When printing on
NAR media, the temperature setting is very important, and we s est an optimum printing condition of 25°C, 50%.
Test Method:
ü Gross Degree:
Use a triangle gloss tester ,setting 60°，given testing data is surface gloss of products.
ü Initial adhesion:
According to testing method (FTM-9,FINAT),remove release liner ,adhesive surface up ,make the specimen annular, to test peeling strength after a quick, complete touch between the specimen and glass.
ü 180°Peel strength(steel,24h):
(FTM-1, FINAT) is measured by peeling a specimen at a 180° angle from a stainless steel or float glass panel, 24 hours after the specimen has been applied under standardized conditions. Initial adhesion is measured 20 minutes after application of the specimen.
ü Dimensional stability:
(FTM-14, FINAT)Is measured on a 150 x 150 mm aluminum panel to which a specimen has been