Description
ST-ZJ 102is composed of ST-ZJ 102B(subsidiary). ST-ZJ 102 ST-ZJ 102B, subsidiary, is mixed by some organic and inorganic material. The cement slurry, composed of ST-ZJ102A and apt ST-ZJ102B, have more excellent performance,such as little fluid loss, zero vertical free water and no retardation effect, quickly developed early strenth. It is s ested to be used together with SW series dispersant, retarder and early strength admixture, so as to get slurry meet the operating standards. Both fresh water and seawater can be used in the slurry. What’s more ,it can resist 5~10% mud contamination. Especially suitable to be used in offshore oil well cementing or areas without dry blending facilities.A,main,is one kind of water-soluble polymer.A(main) and ST-ZJ 102
ST-ZJ 102 can be applied to API G class and J class cement. Mixed with density adjustor, such as microsphere, bentonite, flyash, ilmenite, barite, it could be mixed into different density.
Properties
1. Density: ST-ZJ 102A: 1.02~1.05 g/cm3 ; ST-ZJ 102B : 1.26~1.30 g/cm3
2. Appearances: ST-ZJ 102A:liquid; ST-ZJ 102B:liquid; ST-ZJ 102BS : powder
1. Colors: ST-ZJ 102A :yellowish ; ST-ZJ 102B: light brown; ST-ZJ 102BS: light brown;
3. Smells: none
4. Temperature range : 30~120℃
5. Dosage : ST-ZJ 102A :3.0~6.0%（BWOC）; ST-ZJ 102B(SWJ-5BS): 0.5~1.5%（BWOC）;
7. Package: 25 kg per barrel or sack or as customized
7. Validity: 3 years
Lab test parameters
Table 1Lab test slurry parameters of slurry made from ST-ZJ 102
|
Item
|
Parameters
|
|
Fluid loss，ml（72℃，6.9MPa，30min）
|
≤50
|
|
Thickening time，min (72℃，54.8MPa)
|
>60
|
|
Initial consistence，Bc
|
≤30
|
|
Compressive strength，MPa（95℃，20.7MPa，24h)
|
≥14
|
|
Free water，%
|
≤1.5
|
|
Slurry formula：API Class G cement(HSR)：792g， distilled water：322g，
ST-ZJ102A ：32g, ST-ZJ102B：6.4g, ST-ZJ102BS：2.4g。
|