GREEN SILICON CARBIDE
Green Silicon Carbide is an extremely hard (Knoop 2600 or Mohs 9.4) man made mineral that possesses high thermal conductivity
(100 W/m-K). It also has high strength at elevated temperatures (at 1000°C, Green SiC is 7.5 times stronger than Al2O3). Green SiC has a modulus of elasticity of 410 GPa, with no decrease in strength up to 1600°C, and it does not melt at normal pressures but instead dissociates at 2815.5°C. .
PHYSICAL PROPERTIES
|
Specific Weight |
3.95 g/ cm3 |
|
Mohs Hardness |
9.5 |
|
Maximum service temperature |
1900℃ |
|
Melting Point |
2250℃ |
1,Used for abrasives,blasting,grinding,ceramic,rust removal,surface treatment,
floor coating,abrasion resistant layer etc
|
SiC |
Fe2O3 |
F.C |
F.Si |
SiO2 |
LOI |
|
≥99.0 |
≤0.10 |
≤0.20 |
≤0.20 |
≤0.50 |
< 0.05 |
|
F8 |
+4000um |
0 |
+2800um |
≤20% |
+2360um |
≥45% |
+2360+2000um |
≥70% |
-1700um |
≤3% |
|
F10 |
+3350um |
0 |
+2360um |
≤20% |
+2000um |
≥45% |
+2000+1700um |
≥70% |
-1400um |
≤3% |
|
F12 |
+2800um |
0 |
+2000um |
≤20% |
+1700um |
≥45% |
+1700+1400um |
≥70% |
-1180um |
≤3% |
|
F14 |
+2360um |
0 |
+1700um |
≤20% |
+1400um |
≥45% |
+1400+1180um |
≥70% |
-1000um |
≤3% |
|
F16 |
+2000um |
0 |
+1400um |
≤20% |
+1180um |
≥45% |
+1180+1000um |
≥70% |
-850um |
≤3% |
|
F20 |
+1700um |
0 |
+1180um |
≤20% |
+1000um |
≥45% |
+1000+850um |
≥70% |
-710um |
≤3% |
|
F22 |
+1400um |
0 |
+1000um |
≤20% |
+850um |
≥45% |
+850+710um |
≥70% |
-600um |
≤3% |
|
F24 |
+1180um |
0 |
+850um |
≤25% |
+710um |
≥45% |
+710+600um |
≥65% |
-500um |
≤3% |
|
F30 |
+1000um |
0 |
+710um |
≤25% |
+600um |
≥45% |
+600+500um |
≥65% |
-425um |
≤3% |
|
F36 |
+850um |
0 |
+600um |
≤25% |
+500um |
≥45% |
+500+425um |
≥65% |
-355um |
≤3% |
|
F46 |
+600um |
0 |
+425um |
≤30% |
+355um |
≥40% |
355+300um |
≥65% |
-250um |
≤3% |
|
F54 |
+500um |
0 |
+355um |
≤30% |
+300um |
≥40% |
+300+250um |
≥65% |
-212um |
≤3% |
|
F60 |
+425um |
0 |
+300um |
≤30% |
+250um |
≥40% |
250+212um |
≥65% |
-180um |
≤3% |
|
F70 |
+355um |
0 |
+250um |
≤25% |
+212um |
≥40% |
+212+180um |
≥65% |
-150um |
≤3% |
|
F80 |
+300um |
0 |
+212um |
≤25% |
+180um |
≥40% |
+180+150um |
≥65% |
-125um |
≤3% |
|
F90 |
+250um |
0 |
+180um |
≤20% |
+150um |
≥40% |
+150+125um |
≥65% |
-106um |
≤3% |
|
F100 |
+212um |
0 |
+150um |
≤20% |
+125um |
≥40% |
+125+106um |
≥65% |
-75um |
≤3% |
|
F120 |
+180um |
0 |
+125um |
≤20% |
≥40% |
≥40% |
+106+90um |
≥65% |
-63um |
≤3% |
|
F150 |
+150um |
0 |
+106um |
≤15% |
+75um |
≥40% |
+75+63um |
≥65% |
-45um |
≤3% |
|
F180 |
+125um |
0 |
+90um |
≤15% |
+75um |
* |
+75+63um |
≥40% |
-53um |
* |
|
F220 |
+106um |
0 |
+75um |
≤15% |
+63um |
* |
+63+53um |
≥40% |
-45um |
* |
2.Used for Grinding,polishing,lapping,whetstone,polishing pads,ceramic membrance etc
TYPICAL CHEMICAL ANALISIS [%]
|
SiC |
Fe2O3 |
F.C |
F.Si |
SiO2 |
LOI |
|
98.0-99.5 |
≤0.15 |
≤0.30 |
≤0.40 |
≤0.70 |
< 0.09 |
APARTICLE SIZE DISTRIBUTION
CHAPTER Ⅰ（JIS STANDARD）
|
Size |
DO(um) |
D3(um) |
D50(um) |
D94(um) |
|
#240 |
≤127 |
≤103 |
57.0±3.0 |
≥40 |
|
#280 |
≤112 |
≤87 |
48.0±3.0 |
≥33 |
|
#320 |
≤98 |
≤74 |
40.0±2.5 |
≥27 |
|
#360 |
≤86 |
≤66 |
35.0±2.0 |
≥23 |
|
#400 |
≤75 |
≤58 |
30.0±2.0 |
≥20 |
|
#500 |
≤63 |
≤50 |
25.0±2.0 |
≥16 |
|
#600 |
≤53 |
≤41 |
20.0±1.5 |
≥13 |
|
#700 |
≤45 |
≤37 |
17.0±1.5 |
≥11 |
|
#800 |
≤38 |
≤31 |
14.0±1.0 |
≥9.0 |
|
#1000 |
≤32 |
≤27 |
11.5±1.0 |
≥7.0 |
|
#1200 |
≤27 |
≤23 |
9.5±0.8 |
≥5.5 |
|
#1500 |
≤23 |
≤20 |
8.0±0.6 |
≥4.5 |
|
#2000 |
≤19 |
≤17 |
6.7±0.6 |
≥4.0 |
|
#2500 |
≤16 |
≤14 |
5.5±0.5 |
≥3.0 |
|
#3000 |
≤13 |
≤11 |
4.0±0.5 |
≥2.0 |
|
#4000 |
≤11 |
≤8.0 |
3.0±0.4 |
≥1.8 |
|
#6000 |
≤8.0 |
≤5.0 |
2.0±0.4 |
≥0.8 |
|
#8000 |
≤6.0 |
≤3.5 |
1.2±0.3 |
≥0.6 |