Coated BOPP film Supply Of PET Release Liner PET film manufacturers in china
Specifications:
|
Thickness(micron) |
Width(mm) |
Core ID(inch) |
|
23-50 |
500~2000 |
3”or 6” |
|
The specifications can be adjusted according to the customers’ requirements. |
||
Typical Values:
|
Property |
Unit |
Typical value |
Testing Method |
|
Thickness |
mm |
45 |
DIN 53370 |
|
Tensile Strength（MD/TD） |
MPa |
140/277 |
ASTM D 882 |
|
Elongation at break（MD/TD） |
% |
202/40 |
ASTM D 882 |
|
Heat shrinkage（MD/TD）150℃,30min |
% |
3.0/0.2 |
ASTM D 1204 |
|
Haze |
% |
2.5 |
ASTM D 1003 |
|
Gloss（45°） |
% |
90 |
ASTM D 2457 |
The above values of the properties obtained in our laboratory test. These values are for informative purpose and not in guarantee or warranty in any specific condition. Users are advised to conduct their own testing to determine product suitability to use.
Main characteristics:
In addition to sharing the extraordinary chemical and physical properties owned by the ordinary polypropylene film, this Coated BOPP film also has its unique performances:
1. It is also known as PP crystal film label for its high transparency.
2. Convenient for labelling, sharing the flexibility with PP film, and no edge lifting when squeezed, this product also has a better stiffness and label-taking-off performance than PE film, which can improve the labelling efficiency.
3. The top-coating side of this product has superior printing ink adhesion for UV ink printing and bar code printing on labels, when the other side has improved gelatinizing adhesion, which can make sure there is no glue transfer.
Application:
It is used as face stock of transparent self-adhesive label, such as bottle water & top-grade beer & home care products & personal care products.