Designation:
A743/A743M-13a Standard Specification for Castings, Iron-Chromium, Iron-Chromium-Nickel, Corrosion Resistant, for General Application
A451ASTM A451-06 Standard Specification for Centrifugally Cast Austenitic Steel Pipe for High-Temperatu
A487 Standard Specification for Steel Castings Suitable for Pressure Service
A351 Standard Specification for Castings, Austenitic, for Pressure-Containing Parts
A352 Standard Specification for Steel Castings, Ferritic and Martensitic, for Pressure-Containing Parts, Suitable for Low-Temperature Service
A703 Standard specification for steel casting,General requirements,for pressure-containing parts
Features:
1. High abrasion resistance
2. Corrosion resistance
3. Tear resistance
4. Hardness
Applications:
1. Roller screen rolls for the iron ore pelletizing industry
2. Subsequent pellet processing operation in the steel industry
|
Results of materials testing |
|||||||||
|
Chemical Analysis (%) |
|||||||||
|
Pipe No. |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
|
|
CA6NM |
≤0.06 |
≤1.00 |
≤1.00 |
≤0.04 |
≤0.03 |
3.5-4.5 |
11.5-14.0 |
0.4-1.0 |
|
|
ZG06Cr13Ni4Mo |
≤0.06 |
≤0.80 |
≤1.00 |
≤0.035 |
≤0.025 |
3.5-5.0 |
11.5-13.5 |
0.4-1.0 |
|
|
Mechanical Properties |
||||||
|
Pipe No. |
Heat No. |
Tensile Strength MPa |
Yield Strength
|
Elongation After Fracture % |
Reduction of Area % |
Hardness (HB) |
|
CA6NM |
min. 755 |
min. 550 |
Min. 15 |
Min. 35 |
285HB +-25 |
|
CA6NM stainless steel pipe not only has good corrosion resistance, weldability, but also has high strength and low temperature toughness . CA6NM belongs to low carbon martensite stainless steel, mainly used for hydropower facilities and mine facilities of the wear parts. Such as turbine blades, turbine, roller screen/feeder.
Not only to undergo general corrosion medium, but also to endure the erosion of the sediment, cavitation erosion at runtime. Poor use conditions.