Cross-linking Agent TAIC
Chemical name Triallylisocyanurate
1,3,5-tri(prop-2-en-1-yl)-1,3,5-triazinane-2,4,6-trione
Structural formula
Molecular formula C12H15N3O3
Molecular Weight 249.27
CAS NO 1025-15-6
EINECS No.:213-834-7
TAIC|crosslinking agent TAIC|Donmei TAIC|Powdering TAIC|PERKALINK 301|Sartomer SR533R|Evonik Degussa TAICROS|Japan Asahi Kasei TAIC|PL400|TMPTMA|Fast Cooker|Bridge Agent|VULCOFAC TAIC|タイク |タイク?-M60|トリアリルイソシアヌレート|Accelerator TAIC|DOIE YC-101| Photosensitizer| Vulcanizing agent| Modifier| Intermediate TAIC

Specifications
Item Specifications
Liquid 99 Liquid 98 Liquid 96 Solid
Appearance Colorless transparent liquid or crystal Almost colorless transparent liquid or crystal Yellowish oily liquid or crystal White powder or lumps
Content,% ,≥ 99.0 98.0 96.0 ¬—
Residue on ignition ,% ,≤ — — — 30
Bromine value — — 183-188 —
Acid value(mg KOH/g),≤ 0.2 0.5 1.0 —
crosslinking agent TAIC ,Insoluble Sulfur can improve the resistance to both fatigue and ageing of all kinds of rubber products. It is used as the best vulcanizing agent for rubber. And it is widely used in the manufacture of the rubber chemistry such as tire, rubber pipe, shoes, cable and wire, insulating materials, latex, and all kinds of automobile rubber parts, especially for radial tires.
Advantages of Insoluble Sulfur:
The rubber no need spout frost during storage time. The Insoluble Sulfur is able to keep the unanimous features of the rubber material, and prevent the pollution to rubber product and the models.
With Insoluble Sulfur, there will be no transferring phenomenon between rubber layers that protects the moulding stickiness of the surfaces.
Reduce coking while mix smelting and storage .
Shorten vulcanization time, reduce the dose of sulfur and improve the property of anti-aging of the product.

Crosslinking TAIC modifiers for various thermoplastics (polyethylene, polyvinyl chloride, chlorinated polyethylene, EVA, polystyrene, etc.). Thermal crosslinking is generally added in an amount of 1-3%. Additional dicumyl peroxide (DCP) is 0.2-1%. The amount of irradiation cross-linking is 0.5-2%, and DCP can no longer be added. After cross-linking, the heat resistance, flame retardancy, solvent resistance, mechanical strength and electrical properties of the product can be significantly improved. It is cross-linked by using a peroxide system alone, and the product quality is remarkably improved without odor. Typical for polyethylene, polyethylene / chlorinated polyethylene, polyethylene / EVA cross-linked cable and polyethylene high and low foam products.
ethylene propylene rubber, various fluoro rubber, CPE and other special rubber vulcanizing agent (combined with DCP, the general dosage is 0.5-4%), can significantly shorten the curing time, improve strength, wear resistance, solvent resistance and resistance Corrosive.
 acrylic acid, styrene-type ion exchange resin cross-linking agent, which is less than the divinylbenzene cross-linking agent, high quality, can be prepared to resist pollution, high strength, large pore strength, heat resistance, acid and alkali resistance, An ion exchange resin with excellent properties such as oxidation. This is a new type of ion exchange resin that has been newly developed at home and abroad and has excellent prospects.
Modifiers such as polyacrylate and polyalkyl acrylate can significantly improve heat resistance, optical properties and processability, and are typically used for heat-resistant modification of common organic glass.
 epoxy resin, DAP (polyphthalate propylene glycol) resin modifier, can improve heat resistance, adhesion, mechanical strength and dimensional stability. Typically used for the modification of epoxy potting compounds and encapsulants.
Crosslinking agents and modifiers of unsaturated polyester and thermoplastic polyester can significantly improve heat resistance, chemical corrosion resistance, dimensional stability, weather resistance and mechanical properties. It is typically used to increase the temperature of hot-pressed unsaturated polyester FRP products up to 180 °C.
TAIC itself homopolymer-polytriallyl isocyanurate is a resin with excellent transparency, hardness, heat resistance and electrical insulation, which can be used for bonding glass and ceramics. Typically used to make multi-layer safety glass.
TAIC and emulsion graft copolymerization of acrylic acid, styrene, acrylonitrile, etc., can prepare excellent impact modifiers of thermoplastics such as PVC and PS, and can also directly prepare molded plastics with excellent impact resistance.
9. Metal heat-resistant, radiation-resistant and weather-resistant protective agent. TAIC prepolymer is baked on metal surface. Its baking coating has excellent heat resistance, radiation resistance, weather resistance and electrical insulation. It is typically used to make insulating materials such as printed wiring boards for microelectronic products.
10. Intermediates such as photocurable coatings, photoresists, flame retardants, and flame retardant crosslinkers. Typically used to synthesize high efficiency flame retardant TBC and flame retardant crosslinker DABC.