| Model: | As requirement |
|---|---|
| Brand: | Lite |
| Origin: | Made In China |
| Category: | Metallurgy , Mining & Energy / Metallurgy & Mining / Non-metallic Mineral Products |
| Label: | sillica brick , sillica fire brick , sillica tile |
| Price: |
US $160
/ Ton
|
| Min. Order: | 1 Ton |
| Live Chat: | Last Online:04 Jul, 2017 |
What is the details of our sillica brick?
1.Made by quartz stone materials;
2The content of SiO2 is above 93%;the more SiO2,the higher refractoriness.
3.Al2O3,TiO2 etc impurity amount is under 2%.
What is the Technique Data of our sillica brick?
|
General silica brick:used for coke oven, glass smelting kiln furnace,steel furnace etc . |
||||
|
Item |
GZ-96 |
GZ-95 |
GZ-94 |
GZ-93 |
|
SiO2 % ≥ |
96 |
95 |
94 |
93 |
|
Fe2O3 % ≤ |
1.0 |
1.2 |
1.4 |
1.6 |
|
Refractoriness °C ≥ |
1710 |
1710 |
1710 |
1690 |
|
Apparent porosity % ≤ |
22 |
22 |
23 |
25 |
|
Cold crushing strength Mpa ≥ |
29.4 |
29.4 |
24.5 |
19.6 |
|
Refractoriness under load, 0.2MPa, °C ≥ |
1660 |
1650 |
1640 |
1620 |
|
True density g/cm3 ≤ |
2.34 |
2.37 |
2.38 |
2.39 |
|
Silica brick for Hot-blast stove |
||
|
Item |
Dome wall brick |
Checker brick |
|
SiO2 % ≥ |
95 |
95 |
|
Cold crushing strength Mpa ≥ |
35 |
30 |
|
Apparent porosity % ≤ |
22 |
23 |
|
Creep rate(0.2MPa,1550°C,50h)% ≤ |
0.8 |
0.8 |
|
True density g/cm3 ≤ |
2.35 |
2.35 |
|
Thermal expansion(1000 °C)% ≤ |
1.26 |
1.26 |
|
Silica brick for coke oven |
||
|
Item |
Furnace bottom,Furnace wall |
Other |
|
SiO2 % ≥ |
94 |
94 |
|
Cold crushing strength Mpa ≥ |
30 |
25 |
|
Apparent porosity % ≤ |
22. |
24 |
|
Refractoriness under load, 0.2MPa, °C≥ |
1650(Cementation silica 1620) |
1650(Cementation silica 1620) |
|
Permanent linear Change 1450 °C,2h ≤ |
0-+0.2 |
0-+0.2 |
|
True density g/cm3 ≤ |
2.34 |
2.35 |
|
Thermal expansion(1000 °C)% ≤ |
1.28 |
1.30 |
|
Silica brick for Glass kiln |
|||
|
Item |
XBG-96 |
ZBG-96 |
DBG-96 |
|
Weight/kg |
≤15 |
15-≤25 |
25-≤40 |
|
SiO2 % ≥ |
96 |
96 |
96 |
|
Fe2O3 % ≤ |
0.9 |
0.9 |
1.0 |
|
Melt index % |
0.5 |
0.5 |
0.6 |
|
Apparent porosity % ≤ |
22 |
23 |
24 |
|
Refractoriness under load, 0.2MPa, °C ≥ |
1680 |
1680 |
1670 |
|
Reheating Linear Change(1450 °C,2h) /% ≤ |
0.3 |
0.3 |
0.3 |
|
True density g/cm3 ≤ |
2.34 |
2.34 |
2.35 |
|
Cold crushing strength Mpa ≥ |
35 |
30 |
30
|
What is the Feature of our sillica brick?
1.Good acid erosion resistance.
2.Refractoriness 1690-1730°C.
3.Higher refractoriness under load,above 1620-1680°C.
4.Poor Thermal shock resistance,should not be used for the zone which temperature has rapid change.
5.Poor Volume stability at high temperature,must set aside appropriate expansion joint when laying brick.
6.Generally True density is changed between 2.33-2.42g/cm3,the smaller, the better.
What is the Applications of our sillica brick?
1.Coke oven,blast furnace hot blast furnace,copper smelting furnace,glass smelting kiln furnace,electric furnace roof.
2.Mainly used in the construction of regenerative chamber wall,chimney flue,combustion chamber, coking chamber, furnace roof etc. parts of the coke ovens.
3.Also used in hot blast stove/furnace of dome,furnace wall and checker brick.
4.Steel open hearth of regenerative chamber and sediment chamber,soaking furnace, glass melting furnace and ceramic firing kiln and kiln of the vault etc.