our main product is zirconia cermac blocks,including white blocks and pre-shaed blocks,for white blocks ,inckuding HT(1200Mpa strength,41%translucency),ST(900Mpa strength,44%translucency),SST(600Mpa,strength,49%translucency), our Pre-shaded block includes STC(900Mpa strength,44%translucency),SSC(600Mpa strength,49%translucency) ,High strength HTC(1200Mpa,41% translucency),A1&A2 color fro you choice ,it is suitable for making coping,Thickness:10mm,12mm,14mm,16mm,18mm,20mm,22mm,24mm,25mm ,Diameter :98mm,95mm(Zirconzahn system)and AG71(Amman girrbach system) which type interested ?
Chemical components:
| Compositions | ZrO2+HFO2+Y2O3 | ≥99% |
| Y2O3 | ≤6.0% | |
| HFO2 | <5.0% | |
| Al2O3 | <0.5% | |
| Other oxides | <0.5% |
Technical parameters:
| density before sintering | >3.15±0.05g/cm³ |
| density after sintering | >6.0g/cm³ |
| linear expansion coefficient | (10.3±05)x10‾6K‾¹ |
| three point bending strength | 900mpa,600mpa,1200mpa |
| tyanslucency | 44%,44%,49%,41%-55% |
| chenical solubility after sintering | <100µg/cm² |
| cytotoxicity test |
Cytotoxicity 0 level |
| redioactivity after sintering | <0.1Bq/g |
| sintering temperature | 1480~1530°c,1520ºc is recommend |