| Model: | KLAI-102 |
|---|---|
| Brand: | Kailai |
| Origin: | Made In China |
| Category: | Construction & Decoration / Waterproof Materials |
| Label: | Waterproof membrane , waterproof sheet |
| Price: |
-
|
| Min. Order: | - |
| Live Chat: | Last Online:22 Jun, 2016 |
Kailai Self-adhesive polymer modified bituminous waterproof coiled material is composed of base material, including synthetic rubber like SBS, good heavy-duty road asphalt. The surface is coated by PE film, fine sand,aluminum foil film,and the silicon depositing release film or crepe paper is covered on the lower surface as anti-sticking layer.
-Classified by filler base: without filler(N),Polyester filler (PY)
-N lassified by upper surface isolation materials: Polyethylene film (PE), Polyester film (PET) and Double-sided self-adhered without film (D).
·PY Classified by upper surface isolation materials: Polyethylene film (PE),Fine sand (S) and Double-sided self-adhered without film (D).
·Classified by the physical and mechanical properties:Type Ⅰ and Type Ⅱ .
*Width :1000mm
*Length:10m,15m, 20m,30m.
*Thickness:-N:1.2mm,1.5mm,2.0mm
-PY:2.0mm,3.0mm,4.0mm
2.Feature
1)Excellent flexibility elongation,strong adaptability for substrate shrinkage, deformation and cracks;
2)Available for wet ground,low requirement for basic level,short construction period.
3)Lasting bonding and sealed performance;
4)Excellent adhesive properties, ,self adhesive joints with coil with life;
5)Strong self healing ability for penetration and cracks;
6)Excellent adhesive performance guarantees the integrity of waterproof layer,so as to prevent the occurrence of water channeling phenomenon
7)Safe application for low temperature,no pollution.
3.Technical Index
Type N (without base)
|
NO |
Test Item |
Technical Index |
|||||
|
PE |
PET |
D |
|||||
|
Ⅰ |
Ⅱ |
Ⅰ |
Ⅱ |
||||
|
1 |
Tensile property |
Pull(N/50mm) ≧ |
150 |
200 |
150 |
200 |
|
|
Elongation Max /% ≧ |
200 |
30 |
- |
||||
|
Asphalt break elongation /% |
250 |
150 |
450 |
||||
|
2 |
Nail tear resistance / N ≧ |
60 |
110 |
30 |
40 |
- |
|
|
3 |
Heat resistance |
70 ℃ sliding less than 2mm |
|||||
|
4 |
Low temperature flexibility / ℃ |
-20 |
-30 |
-20 |
-30 |
-20 |
|
|
No crack |
|||||||
|
5 |
Peel strength (N/mm) |
Membrane and aluminium sheet |
1 |
||||
|
Membrane and aluminium sheet |
1.5 |
||||||
|
6 |
Persistent adhesivity / min ≧ |
|
20 |
||||
Type PY (with polymer base)
|
NO |
Test Item |
Technical Index |
|||
|
Ⅰ |
Ⅱ |
||||
|
1 |
Soluble content(g/m2) |
2mm |
1300 |
- |
|
|
3mm |
2100 |
||||
|
4mm |
2900 |
||||
|
2 |
Tensile property |
Pull(N/50mm) ≧ |
2mm |
350 |
- |
|
3mm |
450 |
600 |
|||
|
4mm |
450 |
800 |
|||
|
Elongation Max /% ≧ |
|
30 |
40 |
||
|
3 |
Heat resistance |
70 ℃,no flowing,no dripping |
|||
|
4 |
Low temperature flexibility / ℃ |
-20 |
-30 |
||
|
No crack |
|||||
|
5 |
Peel strength (N/mm) |
Membrane and aluminium sheet |
1 |
||
|
Membrane and aluminium sheet |
1.5 |
||||
|
6 |
Persistent adhesivity / min ≧ |
15 |
|||
|
7 |
Self-adhering asphalt re-peel strength (N/mm) |
1.5 |
|||
4.Application Range
(1)(PE)Self-adhering polymer modified bituminous waterproof sheets is widely used for
* non exposed level, underground and indoor engineering;
*cut-and-cover metro,tunnel,pool,canal and etc.
*Especially in the waterproof engineering can not use open flame.
(2)The upper surface which is coated by aluminum foil film and fine sand is widely used for exposed waterproof engineering.
(3)Double-sided self-adhered sheet is widely used for pre-laid and assistant waterproof,
It can also compound with variety of materials to form multiple waterproof system.