Features and Main application:
a) YRK4A Magnesium hydroxide fire-retardant is high purity Mg(OH)2,,the surface is specially treated with compound vinyl silane.
b) because surface is after organic reaction,so it greatly reduces surface energy, and improves the dispersion and liquidity in organic matter accordingly,
c) as a no halogen flame retardant,it can be used in plastic. such as PE,PP EPDM ,Rubber.Low smoke density and high thermal stability. initial degradation temperature is about 340 degrees centigrade.No Poisonous and causticity air when degradation.
d) Because of compound vinylsilane surface treatment,it is good for improving the compatibility of polymer and filler when casting mold and modification.
e) With pretreatment of powder when chemical reaction,it will deduce clients’ input for facility and processing steps.further Lower the cost of facility and labor
Storage and instructions:
Keep it in dry environment with room temperature
Package:
Standard:25 kgs/bag, plastic woven bag lined with polyethylene plastic bags
Or according to customers’ request
Technical parameters:
|
physical status |
white powder |
|
Mg(OH)2 |
95.1% |
|
CaO |
≤0.79% |
|
Fe2O3 |
≤0.22% |
|
Whiteness |
≥96 |
|
drying shrinkage(120℃,1h) |
0.05% |
|
D50(particle size) |
2.5-4μm |
|
insoluble matter in hydrochloric acid |
0.006% |
|
loss on ignition(900℃) |
≤30% |
|
mohs hardness |
2.5 |
|
Initial dehydration temperature |
340℃<span "="" style="font-size: 9pt;">
|