| Model: | - |
|---|---|
| Brand: | BPM |
| Origin: | Made In China |
| Category: | Construction & Decoration / Waterproof Materials |
| Label: | waterproofing liner , hdpe geomembrane of , for pond and lake da |
| Price: |
US $1.6
/ sq.m
|
| Min. Order: | 5000 sq.m |
| Live Chat: | Last Online:10 May, 2016 |
**Details
BPM waterproofing geomembrane is made from high grade Polyethylene raw material,adding
carbon black,antioxidant,anti-aging and UV-resistance component. It adopted the first class
automatic production equipment and three-layer pressing technology. All products are in accor-
dance with GRI and ASTM test standard.
**Feature
**Application
1.Applied to environment projection and sanitation ,water conservancy ,municipal projects ,landscaping ,petrochemical industry ,mining ,salt industry ,agriculture ,aquaculture
2.Applied to landfill and mining
3.Applied to waterproofing lining of dam or canal and anti-pollution of waste plant
**Technical Data(GRI GM13 Virgin material standard)
| Test | Unit | Standard | BMS75 | BMS10 | BMS15 | BMS20 | BMS30 | Test Frequency | |
| Mechanical | Thickness | mm | D5199 | 0.75 | 1.00 | 1.50 | 2.00 | 3.00 | Per roll |
| Properties | Density | g/cc | D1505/D792 | 0.94 | 90,000 kg | ||||
| Tensile Properties | D 6693 | ||||||||
| · yield strength | kN/m | Type IV | 11 | 15 | 22 | 29 | 44 | 9,000 kg | |
| · break strength | kN/m | 20 | 27 | 40 | 53 | 80 | |||
| · yield elongation | % | 12 | 12 | 12 | 12 | 12 | |||
| · break elongation | % | 700 | 700 | 700 | 700 | 700 | |||
| Tear Resistance | N | D 1004 | 93 | 125 | 187 | 249 | 374 | 20,000 kg | |
| Puncture Resistance | N | D 4833 | 240 | 320 | 480 | 640 | 960 | 20,000 kg | |
| Stress Crack Resistance | hr. | D 5397 | 300 hr. | per GRI GM-10 | |||||
| Carbon Black Content | % | D 4218 | 2.0-3.0% | 9,000 kg | |||||
| Carbon Black Dispersion | D 5596 | For 10 different views: 9 in Categories 1 or 2 and 1 in Category 3 | 20,000 kg | ||||||
| Reference | Oxidative Induction Time | min | D 3895 | 100 min. | 90,000 kg | ||||
| Properties | (a) Standard OIT | D 5885 | 400 min. | ||||||
| (b) High Pressure OIT | |||||||||
| Oven Aging at 85°C retained | % | D 5721 | 55% | per each | |||||
| after 90 days | |||||||||
| (a) Standard OIT - % | D 3895 | 80% | formulation | ||||||
| (b) High Pressure OIT - % | D 5885 | ||||||||
| UV Resistance | % | per each | |||||||
| High Pressure OIT - % retained | D 5885 | 50% | formulation | ||||||
| after 1600 hrs | |||||||||
|
|
|||||||||