No-asbestos composite gasket sheet
Other name: Cylinder Head Gasket Sheet, No-asbestos composite sheet, No-asbestos composite beater sheet, Reinforced no-asbestos sheet, No-asbestos reinforced beater sheet.
No-asbestos composite gasket sheet manufactured from no-asbestos beater sheet(asbestos content is about 5%) with mechanically clinched to 0.18 ~ 0.25mm thick carbon steel tanged (perforated) metal sheet - 08F tinplate insert. It is best gasket material for motorcycle and automobile cylinder head gasket.
The construction include:
Available with Both Size Coating Graphite or Silicon Resin.
Available Size:
Thickness: 1.0mm ~ 3.0mm
400mm x 1000mm, 500mm x 1000mm, 500mm x 1200mm, 500mm x 1500mm, 510mm x 1016mm, 1000mm x 1000mm.
Color: Gray, Black, Red, Green.
The other size is optional or according to the requirements of customers.
Technical Date Sheet
| Item | Standard data | |
| Density g/cm³ | 1.3～1.5 | |
| working temperature ℃ | -200～250 | |
| Compressibility % | 15～20 | |
| Recovery ≥ % | 40 | |
| causticity | Cusp no rusty | |
| Tensile strength MPa ≥ | 7.0 | |
| Compressive Strength MPa ≥ | 80.0 | |
| Carbon content ≥ % | 98 | |
| Ash content ＜% | 1 | |
| With the temperature of 150±2℃, Soaking 20# fluid oil for 5 hours, MPa≥ | oil absorption %≤ | 25 |
| Thickness-increasing %≤ | 0～10 | |
| Stripping performance | No stripe | |
| With the temperature of 15 to 30℃, Soaking 75# kerosene for 5 hours, MPa≥ | oil absorption %≤ | 15 |
| Thickness-increasing %≤ | 0～15 | |
| Stripping performance | No stripe | |
| With the temperature of 100℃, Soaking distilled water for 5 hours, MPa≥ | water absorption %≤ | 15 |
| Thickness-increasing %≤ | 0～15 | |
| Stripping performance | No strip
|
|