HDPE TR144 Description |
||
| HDPE TR144 is a copolymer high density polyethylene for film molding. | ||
| Application | ||
| The product is used for making film, packing, bags. | ||
| Total | ||
| Material’s state | •Current valid | |
| Performance characteristics | •Eligibility of food contact | |
| Processing method | •blow molding | |
| Appearance | •White | |
| Application | •film, packing, bags | |
| Physical property | Rating | Test method |
| Density | 0.946g/cm3 | ASTM D-1505 |
| MFR （190℃/2.16kg） | 0.2 g/10min | ASTM D-1238 |
| MFR（190℃/2.16kg(HLMI) ） | 15 g/10min | ASTM D-1238 |
| Mechanical property | Rating | Test method |
| Tensile yield strength（MD） | 26MPa | ASTM D-882 |
| Tensile yield strength（TD） | 25MPa | ASTM D-882 |
| Tensile strength（MD） | 32 MPa | ASTM D-882 |
| Tensile strength（TD） | 31 MPa | ASTM D-882 |
| Elongation at break（MD） | 500% | ASTM D-882 |
| Elongation at break（TD） | 600% | ASTM D-882 |
| Flexural modulus | 1103 MPa | ASTM D-790 |
| Falling dart impact strength | 100 g | ASTM D-1709 |
| Other property | Rating | Test method |
| Typical blown film performance(0.025mm) | blow ratio 4:1 | |
| Elleman, torn apart（MD） | 26 g | ASTM D-1922 |
| Elleman, torn apart（TD） | 410g | ASTM D-1922 |
|
NOTE ISO 9001 2000 |
||
| Typical properties: these are not to be construed as specifications | ||