Features/Applications:
BH-LB4 Made from radiation cross-linked polyolefin and suitable for applications up 1KV. The properties of electrically insulating, UV resistant and weatherproof makes BH-LB4 widely used in electric power industry to provide insulation and seal sealing over the crutch of multi-core cables.
1) Minimum shrink temperature: 110°C
2) Minimum fully recovery temperature: 130°C
3) Standard color: Black
Technical data:
|
Property |
Test Method |
Typical Data |
|
Operating temperature |
IEC 216 |
-55°Cto +110°C |
|
Tensile strength |
ASTM D 2671 |
13 MPa Min |
|
Tensile strength after thermal aging |
ASTM D 2671 (120°C /168hrs) |
10 MPa Min |
|
Elongation at break |
ASTM D 2671 |
300% Min |
|
Elongation at break after thermal aging |
ASTM D 2671 (120°C /168hrs) |
250% Min |
|
Dielectric strength |
IEC 243 |
15KV/mm Min |
|
Volume resistance |
IEC 93 |
1013Ω.cm Min |
|
Water absorption |
ISO62 |
1% Max |
Specification and sizes (mm):
|
Order ref. Number |
As supplied (mm) |
After recovered (mm) |
|||||||
|
D1 (Min.) |
D2 (Min.) |
D1 (Max.)
|
D2 (Max.) |
D3 (mm.) |
L(±10%)
|
F(±10%)
|
W1(±10%) |
W2(±10%) |
|
|
BH-LB410 40/15 |
42 |
14 |
15 |
3.5 |
20 |
105 |
26 |
2.2 |
2 |
|
BH-LB420 55/21 |
55 |
20 |
21 |
5 |
26 |
150 |
40 |
3.1 |
2.6 |
|
BH-LB425 65/26 |
65 |
26 |
26 |
7 |
33 |
175 |
45 |
3.3 |
2.9 |
|
BH-LB430 75/26 |
75 |
28 |
26 |
7 |
33 |
175 |
45 |
3.3 |
2.9 |
|
BH-LB440 82/37 |
82 |
30 |
37 |
9 |
45 |
190 |
60 |
4 |
3 |
|
BH-LB445 90/37 |
90 |
32 |
37 |
9 |
45 |
190 |
60 |
4 |
3 |
|
BH-LB450 100/47 |
102 |
38 |
47 |
12 |
55 |
198 |
58 |
4 |
3 |
|
BH-LB460 125/52 |
130 |
52 |
52 |
15 |
60 |
240 |
75 |
4 |
4 |
|
BH-LB470 160/70 |
160 |
64 |
70 |
19 |
78 |
260 |
75 |
4 |
4 |