| Model: | HY2135 or 2235 |
|---|---|
| Brand: | Hong Ye RTV silicone |
| Origin: | Made In China |
| Category: | Chemicals / Rubber Materials |
| Label: | silicone , Pad Printing Silicon , rtv |
| Price: |
US $12
/ kg
|
| Min. Order: | 200 kg |
| Live Chat: | Last Online:07 Aug, 2014 |
Description
Transparent Silicone Rubber for Resin Diamond Molding for all kinds of jewelry, crystal deocarations molding . It’s generally named two-components silicone rubber which will be cured by heated temperature, Part A is a flowable liquid, part B is the curing agent. It features an exceptional fluidity and good operability. The mixing ratio is 10:1.
Application
Transparent Silicone Rubber for Resin Diamond Molding is rapid prototyping for imitational crystal diamond, resin diamond decorations, also suitable for molding epoxy resin, polyester resin, polystyrene, vinyl, paraffin wax, low melting point alloy, concrete and so on, also used in cultural relics, copy and art crafts.
Technical Parameters
|
Model |
HY 2135 |
HY 2235 |
|
Appearance |
translucent |
transparent |
|
Mixing ratio |
10:1 |
10:1 |
|
Viscosity (CPS) |
70000 |
70000 |
|
Pot life(25°C) |
>2-3h |
>2-3 h |
|
Curing time(°C/mins) |
100-120°C/30mins |
100-120°C/30mins |
|
Density (g·cm-30 |
1.1 |
1.1 |
|
Hardness(A°) |
35 |
35 |
|
Enlongation-break (%) |
≥280 |
≥320 |
|
Tear-strength (KN·m-1) |
≥15 |
≥18 |
|
Tensile-strength (Mpa) |
≥4.8 |
≥5.2 |
|
Retractility (%) |
0.1 |
0.1 |
Characteristics
*Body safe, skin safe, medical grade, nontoxic.
*High tensile and tear strength
*High temperature resistance, can resist more then 250°C
*Easy for operation (mixing ratio at 1:1 /10:1)
*Easy demoulding
*Good dimensional stability
*Rapid prototyping
Shelf life and Transportation
1. Twelve(12) months when stored at 25C in tightly closed original packages.
2. This kind of product is non-dangerous product, which could be transported as general chemicals.