Description
Polyethylene polypropylene/polyester fibre waterproofing roll material is made by multipleply
different materials, especially its ageing and weathering resistance layer enables the membrane
possess more longer effective age. It can bond with many kinds of adhesions, firm and secure.
In case of cement base, cementitious agent can be used, the cementitious agent can easily enter
into the nonwoven felt layer, forms a well combination with cement after solidification, permanent
durability.
Width: 1.15m, 1.2m
Length: 50m, 100m or as required
Thickness: 0.55mm-1.5mm or as required
Material: PP nonwoven laminated with PE film.
Features:
Good tensile strength, excellent elongation, non-toxic, no pollution
This product is composed of extruded PE membrane with polypropylene fiber or Dacron covered
on both sides of the core membrane as reinforced layer to make it big friction and easy to be stuck
firmly to the concrete. With characteristics of easy installation, no pollution and good durability.
Application area:
Polyethylene Polypropylene Waterproof Membrane is used in roofing, basement., restroom, water conservation, warehouse to protect structure from water.
|
Test project |
Standards |
Test result |
||
|
Above1.0 |
Under1.0 |
|||
|
Fracture tensile strength |
Room temperature≥ |
60 |
48 |
Vertical65,horizontal68 |
|
60°C≥ |
30 |
24 |
||
|
Plastic elongation at break |
Room temperature≥ |
400 |
50 |
Vertical672,horizontal665 |
|
-20°C≥ |
10 |
8 |
||
|
N ≥tear strength |
20 |
16 |
Vertical68,horizontal68 |
|
|
30min no leakage impermeability |
0.3Mpa |
|
impermeable |
|
|
°C≤ low bending |
-20 |
|
No crack |
|
|
Expansion rate of heating |
Extend< |
2 |
|
Vertical indent1,horizontal0 |
|
Shrink< |
4 |
|
||
|
Hot air aging(80°C×168H) |
Tensile breaking strength retention rate %≥ |
80 |
|
Vertical95,horizontal 105 |
|
Maintain the rate of plastic elongation at break %≥ |
70 |
Vertical50,horizontal 34 |
||
|
Alkali resistance {10% Ca(OH)2×temperature×168h} |
Tensile breaking strength retention rate %≥ |
80 |
|
Vertical98,horizontal 98 |
|
Maintain the rate of plastic elongation at break %≥ |
80 |
Vertical81,horizontal 71 |
||