| Model: | E-620 silicone |
|---|---|
| Brand: | hong ye silicone |
| Origin: | Made In China |
| Category: | Chemicals / Rubber Materials |
| Label: | cake mold silicone , liquid silicone , rtv mold silicone |
| Price: |
US $12.28
/ pc
|
| Min. Order: | 200 pc |
| Live Chat: | Last Online:04 May, 2014 |
FDA Grade cake mold silicone Description:
FDA Grade cake mold silicone is generally named as two-part addition silicone rubber that vulcanizes at room temperature. Part A is a flowable liquid, part B is the curing agent (platinum catalyst). It features an exceptional fluidity, good operability, excellent physical properties and very low shrinkage. The mixing ratio between Part A and Part B can be 10:1 or 1:1.
FDA Grade cake mold silicone Main application:
FDA Grade cake mold silicone Main properties:
FDA Grade cake mold silicone(25°C)
(The mixing ratio of part A and part B can be adjusted to 1:1or 10:1)
|
Product |
E-615 |
E-620 |
E-625 |
E-630 |
E-642 |
|
Appearance |
Translucent |
Translucent |
Translucent |
Translucent |
Translucent |
|
Hardness(shore A) |
15±2 |
20±2 |
25±2 |
30±2 |
42±2 |
|
Mix ratio(A:B) |
1:1 |
1:1 |
1:1 |
1:1 |
10:1 |
|
Viscosity Part A(mPa.s) |
22000±2000 |
23000±2000 |
27000±2000 |
25000±2000 |
55000±2000 |
|
Viscosity Part B(mPa.s) |
1900±500 |
1900±500 |
1800±500 |
2400±500 |
150±50 |
|
Tensile strength (MPa) |
5.2 |
5.7 |
6.7 |
5.5 |
7.6 |
|
Tear-strength (kN/m) |
25 |
26 |
23 |
24 |
22 |
|
Elongation(%) |
569 |
581 |
480 |
410 |
450 |
|
Density |
1.05 |
1.05 |
1.07 |
1.13 |
1.14 |
|
Pot life/working time (mins) |
30-40 |
30-40 |
30-40 |
30-40 |
30-40 |
|
Curing time/setting time (hrs) |
3-4hrs(25°C) 120-30mins(60°C) |
3-4hrs(25°C) 120-30mins(60°C) |
3-4hrs(25°C) 120-30mins(60°C) |
3-4hrs(25°C) 20-30mins(60°C) |
6-8hrs(25°C) 130-50mins(60°C) |
|
Shrinkage rate (%) |
0.1 |
0.1 |
0.1 |
0.1 |
0.1 |
Notice:
All above addition silicone is forbidden to mix with organic compounds of condensation cure silicone rubber; otherwise, the silicone rubber will not cure, and also should not mix with organic compounds containing S, P, N as well as metallic salt of organic acids. It also will cause this product cure incompletely or not cure.
For getting further information about addition silicone rubber, PLS contact with