Product
|
Type
|
Range of application
|
|
Composite portland cement
|
32.5,32.5R
|
For ordinary civil and public constructions, real estate and hydraulic engineering. Especially for ordinary prefabricated parts and concrete, also for building mortar, masonry, marble inlaying, tiling etc
|
|
Ordinary portland cement
|
42.5,42.5R
|
For important structure high strength concrete and prestressed concrete project, like as bridge, wharf, road, airport, high rise building and other large concrete construction works, and also for ordinary industrial and civil construction engineering.
|
|
Portland cement
|
52.5,52.5R
|
For high strength concrete and prefabricated parts, like as road, bridge, etc
|
|
Packaging
|
50kg per bag, 40 bags into a 2MT jumbo bag; or as your requirements
|
|
|
Portland cement
|
32.5
|
32.5R
|
||||
|
Items
|
Units
|
National
|
Internal
|
National
|
Internal
|
|
|
Sample size
|
Kg
|
/
|
5.0
|
/
|
5.3
|
|
|
SO3
|
%
|
3.5
|
2.4
|
3.5
|
2.5
|
|
|
MgO
|
%
|
6.0
|
1.1
|
6.0
|
1.4
|
|
|
Cl
|
%
|
0.06
|
0.01
|
0.06
|
0.01
|
|
|
Fineness
(residue on sieve, 80m)
|
%
|
10.0
|
0.2
|
10.0
|
0.2
|
|
|
Time
|
Initial
|
H:Min
|
0:45
|
4:50
|
45
|
228
|
|
Final
|
H:Min
|
10:00
|
5:45
|
600
|
368
|
|
|
Soundness pat test
|
/
|
past
|
/
|
past
|
||
|
Bending strength
|
3d
|
MPa
|
2.5
|
4.8
|
3.5
|
4.8
|
|
28d
|
MPa
|
5.5
|
7.3
|
5.5
|
7.5
|
|
|
Compressive
strength
|
3d
|
MPa
|
10.0
|
25.4
|
15.0
|
22.8
|
|
28d
|
MPa
|
32.5
|
42.2
|
32.5
|
43.6
|
|
|
Portland cement
|
42.5
|
42.5R
|
||||||
|
Items
|
Units
|
National
|
Internal
|
National
|
Internal
|
|||
|
Sample size
|
Kg
|
/
|
6.0
|
/
|
6.0
|
|||
|
SO3
|
%
|
3.5
|
2.44
|
3.5
|
2.8
|
|||
|
MgO
|
%
|
6.0
|
1.32
|
6.0
|
1.4
|
|||
|
Cl
|
%
|
0.06
|
0.021
|
0.06
|
0.02
|
|||
|
Loss
|
%
|
5.0
|
3.74
|
5.0
|
4.0
|
|||
|
Fineness
(specific surface)
|
/kg
|
300
|
358
|
300
|
385
|
|||
|
Standard consistency water
|
%
|
/
|
28.0
|
/
|
28.0
|
|||
|
Time
|
Initial
|
H:Min
|
0:45
|
4:50
|
45
|
228
|
||
|
Final
|
H:Min
|
10:00
|
5:45
|
600
|
368
|
|||
|
Soundness pat test
|
/
|
past
|
/
|
past
|
||||
|
Bending strength
|
3d
|
MPa
|
3.5
|
5.1
|
4.0
|
6.2
|
||
|
28d
|
MPa
|
6.5
|
8.6
|
6.5
|
9.2
|
|||
|
Compressive
strength
|
3d
|
MPa
|
17.0
|
26.6
|
22.0
|
30
|
||
|
28d
|
MPa
|
42.5
|
50.9
|
42.5
|
52.6
|
|||
|
Portland cement
|
52.5
|
52.5R
|
||||||
|
Items
|
Units
|
National
|
Internal
|
National
|
Internal
|
|||
|
SO3
|
%
|
3.5
|
2.45
|
3.5
|
2.31
|
|||
|
MgO
|
%
|
5.0
|
1.04
|
5.0
|
1.2
|
|||
|
Cl
|
%
|
0.06
|
0.021
|
0.06
|
0.022
|
|||
|
Loss
|
%
|
5.0
|
1.98
|
3.5
|
1.92
|
|||
|
Fineness
(specific surface)
|
/kg
|
300
|
385
|
300
|
391
|
|||
|
Time
|
Initial
|
Min
|
45
|
124
|
45
|
228
|
||
|
Final
|
Min
|
600
|
164
|
600
|
368
|
|||
|
Soundness pat test
|
/
|
past
|
/
|
past
|
||||
|
Bending strength
|
3d
|
MPa
|
4.0
|
6.7
|
5.0
|
7.3
|
||
|
28d
|
MPa
|
7.0
|
9.0
|
7.0
|
9.5
|
|||
|
Compressive
strength
|
3d
|
MPa
|
23.0
|
34.5
|
27.0
|
35.1
|
||
|
28d
|
MPa
|
52.5
|
62.6
|
52.5
|
62.1
|
|||