Model: | PVC-L |
---|---|
Brand: | SD |
Origin: | Made In China |
Category: | Construction & Decoration / Waterproof Materials |
Label: | App. Waterproof memb , pvc waterproof , Pvc tensile membrane |
Price: |
US $2.69
/ ㎡
|
Min. Order: | 3000 ㎡ |
Live Chat: | Last Online:28 Apr, 2016 |
PVC waterproof membranes
with fiber composite backing sheet (code L)
Products Description
The PVC waterproofing rolls formulas are based upon polyvinyl chloride resin with other assistants added to provide flexibility and stability such as anti-oxidant,absorbent of ultraviolet light, plasticizer and plastic filling agent.
Products Specification
Name |
Thickness(mm) |
Width(m) |
Length(m) |
PVC-L |
1.2-2.0 |
2 |
20 |
Physical Properties
PVC Physical Properties GB12953-2003
Item |
Specification |
|||||||
H |
L |
P |
G |
GL |
||||
The resin thickness of Middle fabric,mm≥ |
— |
0.40 |
||||||
Tensile Properties |
Maximum tension N/cm ≥ |
— |
120 |
250 |
— |
120 |
||
Tension strength Mpa≥ |
10 |
10 |
||||||
Maximum tension elongation%≥ |
15 |
|||||||
Fracture elongation,%≥ |
200 |
150 |
200 |
100 |
||||
Heat treatment size change rate,%≤ |
2.0 |
1.0 |
0.5 |
0.1 |
0.1 |
|||
Low-temperature bending |
-25℃No crack |
|||||||
Water tightness |
0.3Mpa,2hNo seepage |
|||||||
Attack resistance |
0.5kg·m,No seepage |
|||||||
static charge resistance |
20kgNo seepage |
|||||||
Seam strip strength,N/mm≥ |
4.0orMembranes break |
3.0 |
||||||
right-angle tear strength,N/mm≥ |
50 |
50 |
||||||
Trapezoid tear strength,N≥ |
150 |
250 |
220 |
|||||
Water absorption(70℃ 168h)% |
After soaking≤ |
4.0 |
||||||
air-cure later≥ |
-0.40 |
|||||||
Heat aging(80℃) |
Time |
672h |
||||||
Appearance |
No blister,flaw,delamination,coherence,hole |
|||||||
Tensile strength retention,%≥ |
85 |
|||||||
Elongation rate of keeping,%≥ |
80 |
|||||||
Low temperature bend |
-20℃No crack |
|||||||
Chemistry resistance |
Appearance |
No blister,flaw,delamination,coherence,hole |
||||||
Tensile strength retention%≥ |
85 |
|||||||
Elongation rate of keeping%≥ |
80 |
|||||||
Low-temperature bending |
-20℃No crack |
|||||||
Artificial weather accelerated aging |
Time |
1500hb |
||||||
Appearance |
No blister,flaw,delamination,coherence,hole |
|||||||
Tensile strength retention%≥ |
85 |
|||||||
Elongation rate of keeping%≥ |
80 |
|||||||
Low temperature bend |
-20℃No crack |
Application Range
PVC membranes form an effective barrier to liquid water or water vapor in the roof construction for industrial and civil engineering, underground engineering such as subway & tunnel, water conservancy such as water pools & ditch, shelter, grain depot, land filling, dyke, sewage treatment and basement.
Payment Terms: | T/T |
---|---|