Model: | STD1260 |
---|---|
Brand: | YUNTAI |
Origin: | Made In China |
Category: | Construction & Decoration / Fire Retardant |
Label: | ceramic fiber wool , ceramic fiber bulk , ceramic fiber |
Price: |
-
|
Min. Order: | - |
Live Chat: | Last Online:25 Mar, 2013 |
COM alumina silicate swinging fiber cotton
ST alumina silicate swinging fiber cotton
HP alumina silicate swinging fiber cotton
HA alumina silicate swinging fiber cotton
HAZ alumina silicate swinging fiber cotton
HZ alumina silicate swinging fiber cotton
2. FEATURE
No lube, no processed, low ball sediment blown fiber is the material filled of high temperature
3. PRODUCTION ENGEERING
COM swinging fiber cotton, adopting Flint Clay as the material, melted by resistance furnace, is produced by swinging technology.
HP, HA swinging fiber cotton, adopting HP Alumina, Silica Powder as the material, melted by Resistance Furnace, is produced by swinging technology.
HZ swinging fiber cotton, adopting HP Alumina, silica powder, zircon, melted by resistance furnace, blowing or swinging, is produced by swinging technology.
4. TECHNICAL FEATURE:
Low thermal conductivity and heat capacity
No corrosive material
Good heat insulation and sound absorption
5. APPLICATION:
Raw material of fiber paper and vacuum forming
Raw material of fiber spray paint and castable
Filler material of high temperature furnace
Raw material of fiber textile
Item | COM | ST | HP | HA | HAZ | HZ | |
Classification Temperature ℃ | 1100 | 1260 | 1260 | 1360 | 1360 | 1430 | |
Working Temperature ℃ | <1000 | 1050 | 1100 | 1200 | 1200 | 1350 | |
Fiber diameter (um) | blowing | 2-3 | 2-3 | 2-3 | 2-3 | 2-3 | 2-3 |
swing | 3-4.5 | 3-4.5 | 3-4.5 | 3-4.0 | 3-4.0 | 3-4.0 | |
Chemical Composition (%) | AL2O3 | 42-44 | 45-46 | 47-49 | 52-55 | 45-46 | 39-40 |
AL2O3+SIO2 | 96 | 97 | 99 | 99 | - | - | |
AL2O3+SIO2 +ZrO2 | - | - | - | - | 99 | 99 | |
ZrO2 | - | - | - | - | 5-7 | 15-17 | |
Fe2O3 | <1.2 | <1.0 | 0.2 | 0.2 | 0.2 | 0.2 | |
Na2O+K2O | ≤0.5 | ≤0.5 | 0.2 | 0.2 | 0.2 | 0.2 |