Home > Products > Metallurgy , Mining & Energy > Metallurgy & Mining > Stainless Steel

Grade:

900 series

Standard:

JIS, AISI, ASTM, GB, DIN, EN

Length:

1000-6000mm or as the customers' requirements

Thickness:

0.3-100mm

Width:

500-3000mm or as the customers' requirements

Place of Origin:

Tianjin China (Mainland)

Brand Name:

hhdy

Model Number:

0286

Type:

Plate

Application:

Industry

Certification:

ISO

Technic:

cold rolled/hot rolled

Trade terms:

FOB , CIF , CFR ect

Surface finish:

2B,BA,ect

Packaging Detail:

In bundles with seaworthy wooden pallets or as per requirement

Delivery Detail:

normally within 10-25 days or based on your quantity

Product Name

stainless steel sheet price 904l 

Standard

 JIS, AISI, ASTM, GB, DIN

Width

 500-3000mm or as the customers' requirements

Length

 1000-6000mm or as the customers' requirements

Thickness

 0.3-100mm

Superiority

 High quality and Competitive price

Third part inspection

 Third part inspection is supported by us

Application

 construction field, ships building industry,
petroleum & chemical industries, war and electricity industries, food processing and medical industry, boiler heat exchanger, machinery and hardware fields ,etc.

Packing

 export standard or as customers' requirement

Delivery time

 about 15 days after the confirmation of the deposit

Payment terms

 L/C or T/T 

Attention

We will supply you good quality and bottom price and first-class service in china and hope to be your golden supplier

C

Cr

Cu

Mn

Mo

Ni

P

S

Si

Max

Max

Max

Max

Max

0.02

19.0-23.0

1.0-2.0

2.0

4.0-5.0

23.0-28.0

0.045

0.035

1.0

Grade

Tensile Strength (MPa) min

Yield Strength 0.2% Proof (MPa) min

Elongation (% in 50mm) min

Hardness

Rockwell B (HR B)

Brinell (HB)

904L

490

220

35

70-90 typical

-

Rockwell Hardness value range is typical only; other values are specified limits.

Grade

Density
(kg/m3)

Elastic Modulus
(GPa)

Mean Co-eff of Thermal Expansion (µm/m/°C)

Thermal Conductivity
(W/m.K)

Specific Heat 0-100°C
(J/kg.K)

Elec Resistivity
(nΩ.m)

0-100°C

0-315°C

0-538°C

At 20°C

At 500°C

904L

8000

200

15

-

-

13

-

500

850