Model: | 002 |
---|---|
Brand: | RUIQI |
Origin: | Made In China |
Category: | Chemicals / Chemical Reagent |
Label: | Tyre Cord Fabric |
Price: |
-
|
Min. Order: | - |
Live Chat: | Last Online:12 Oct, 2012 |
Item
|
Unit
|
Specification(dtex/ plies)
|
|||||
2100/2 (1890D/2)
|
1870/2 (1680D/2)
|
||||||
Best
|
first-class
|
qualified
|
Best
|
first-class
|
qualified
|
||
Breaking Strength
|
N/end
|
313.6
|
303.8
|
294.0
|
279.3
|
269.5
|
259.7
|
Elongation@100N
|
%
|
9.5±0.5
|
9.5±0.8
|
9.5±1.0
|
|
|
|
Elongation@88.2N
|
|
|
|
9.5±0.5
|
9.5±0.8
|
9.5±1.0
|
|
Elongation@66.7N
|
|
|
|
|
|
|
|
Elongation@44.4N
|
|
|
|
|
|
|
|
H-Extraction Test
|
N/cm
|
176.4
|
166.6
|
156.8
|
166.6
|
156.8
|
147.0
|
Uneven in breaking strength
|
%
|
3.8
|
5.0
|
6.3
|
3.8
|
5.0
|
6.3
|
Uneven in Elongation at break
|
%
|
6.3
|
7.5
|
8.8
|
6.3
|
7.5
|
8.8
|
Dip pick up
|
%
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
Elongation at break
|
%
|
23±2.0
|
23±2.0
|
23±2.0
|
23±2.0
|
23±2.0
|
23±2.0
|
Diameter/Gauge
|
mm/10
|
7.8±0.3
|
7.8±0.4
|
7.8±0.5
|
7.8±0.3
|
7.8±0.4
|
7.8±0.5
|
Z- Twist
|
T-m
|
320±15
|
320±15
|
320±15
|
330±15
|
330±15
|
330±15
|
S- Twist
|
320±15
|
320±15
|
320±15
|
330±15
|
330±15
|
330±15
|
|
Heat Shrinkage
|
%
|
6.0
|
6.5
|
7.5
|
6.0
|
6.5
|
7.5
|
Water ratio
|
%
|
1.0
|
1.0
|
1.0
|
1.0
|
1.0
|
1.0
|
Item
|
Unit
|
Specification(dtex/ plies)
|
|||||
1400/3 (1260D/3)
|
1400/2 (1260D/2)
|
||||||
Best
|
first-class
|
qualified
|
Best
|
first-class
|
qualified
|
||
Breaking Strength
|
N/end
|
313.6
|
303.8
|
294.0
|
215.6
|
205.8
|
196.0
|
Elongation@100N
|
%
|
9.5±0.5
|
9.5±0.8
|
9.5±1.0
|
|
|
|
Elongation@88.2N
|
|
|
|
|
|
|
|
Elongation@66.7N
|
|
|
|
9.5±0.5
|
9.5±0.8
|
9.5±1.0
|
|
Elongation@44.4N
|
|
|
|
|
|
|
|
H-Extraction Test
|
N/cm
|
176.4
|
166.6
|
156.8
|
147.0
|
137.2
|
127.4
|
Uneven in breaking strength
|
%
|
3.8
|
5.0
|
6.3
|
3.8
|
5.0
|
6.3
|
Uneven in Elongation at break
|
%
|
6.3
|
7.5
|
8.8
|
6.3
|
7.5
|
8.8
|
Dip pick up
|
%
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
4.5±1.0
|
Elongation at break
|
%
|
23±2.0
|
23±2.0
|
23±2.0
|
23±2.0
|
23±2.0
|
23±2.0
|
Diameter/Gauge
|
mm/10
|
7.8±0.3
|
7.8±0.4
|
7.8±0.5
|
6.5±0.3
|
6.5±0.4
|
6.5±0.5
|
Z- Twist
|
T-m
|
320±15
|
320±15
|
320±15
|
370±15
|
370±15
|
370±15
|
S- Twist
|
320±15
|
320±15
|
320±15
|
370±15
|
370±15
|
370±15
|
|
Heat Shrinkage
|
%
|
6.0
|
6.5
|
7.5
|
6.0
|
6.5
|
7.5
|
Water ratio
|
%
|
1.0
|
1.0
|
1.0
|
1.0
|
1.0
|
1.0
|