Glass Fiber Reinforced Flame Retardant PA66
Product Description
Environmental Bromine Antimony Flame Retardants System, Meets the Requirements of 2002/95/EC and Other Countries' Environmental Directives. Flame Retardance(UL94-V0, 0.75mm).
Characteristic :
l High Mechanical Properties
l Superior Heat Resistant
l Good Dimensional Stability
l Flame Retardant (0.75mm UL94-V0)
l E/E Parts
Molding Recommendation :
|
Pre-dry Condition
|
Injection Temperature
|
Injection Speed
|
Mold Temperature
|
|
80℃(2-3 hours)
|
280-265℃
|
Middle - Fast
|
80-90℃
|
Remark:The molding data is just for reference. The parameter should be changed under difference of mold design, product shot volume, and material resident time.
Property Index:
|
Properties
|
Test Method
|
Units
|
4002G0
|
4002G25
|
|
Glass Fiber Content
|
---
|
---
|
0%
|
25%
|
|
Density
|
ASTM D-792
|
g/cm3
|
1.30
|
1.55
|
|
Melt Index
(275℃/0.325kgs)
|
ASTM D-1238
|
g/10min
|
12
|
9.0
|
|
Heat Deflection Temp (0.45MPa)
|
ASTM D-648
|
℃
|
65
|
235
|
|
Heat Deflection Temp(1.82MPa)
|
ASTM D-648
|
℃
|
65
|
235
|
|
Tensile Strength, yield
|
ASTM D-638
|
MPa
|
80
|
140
|
|
Break Elongation
|
ASTM D-638
|
%
|
22
|
10
|
|
Flexural Strength
|
ASTM D-790
|
MPa
|
115
|
180
|
|
Flexural Modulus
|
ASTM D-790
|
MPa
|
3000
|
6500
|
|
Izod Impact Strength, notched
|
ASTM D-256
|
J/m
|
35
|
130
|
|
CTI
|
IEC60112
|
V
|
550
|
600
|
|
Flammability
|
UL94
|
1.5mm
|
V0
|
V0
|
|
3.0mm
|
V0
|
V0
|
Remark:The data are intended as a general guide only,makes no results and assumes no obligation or liability.
|
Product Image
Img 1
Send Inquiry to this Member
Related Products of this Company
This member assumes full responsibility for the content of this listing. DIYTrade accepts no responsibility whatsoever in respect of such content.
To report fraudulent or illegal content, please
click here.
China Suppliers Quick Searching:
,