Structure |
All-glass double-tube co-axial structure |
|
Glass material |
High borosilicate 3.3 glass |
|
External pip diameter and thickness |
Φ=47±1.0mm§=1.6mm±0.2mm Φ=58±1.0mm§=1.8mm±0.2mm Φ=70±1.5mm§=2.2mm±0.3mm |
|
Internal pip diameter and thickness |
Φ=37±0.8mm§=1.4mm±0.2mm Φ=47±1.0mm§=1.6mm±0.2mm Φ=58±1.0mm§=1.8mm±0.2mm |
|
Pipe length |
950mm 1500mm 1600mm 1700mm 1800mm 1900mm 2000mm 2100mm |
|
Absorptive coating property |
Structure |
Cu/SS-ALN(H)/SS-ALN(L)/ALN |
Sediment method |
3 target magnetron sputtering plating |
|
Specific absorption |
As =0.93~0.96 (AM1.5) |
|
Emission ratio |
εh =0.04~0.06 (80±5) |
|
Vacuum tightness |
P≤5.0×10-3Pa |
|
Idle sunning property parameters |
Y=260~300 m2.C/KW |
|
Solar irradiation for obtaining a preset water temperature |
H≤4.7MJ/m2(Φ58) |
H=3.7~4.2 MJ/m2 |
H≤3.7MJ/m2(Φ47) |
H=2.9~3.2 MJ/m2 |
|
Average heat loss coefficient |
ULT=0.4~0.6W/(m2.) |
Structure |
All-glass double-tube co-axial structure |
|
Glass material |
High borosilicate 3.3 glass |
|
External pip diameter and thickness |
Φ=47±1.0mm§=1.6mm±0.2mm Φ=58±1.0mm§=1.8mm±0.2mm Φ=70±1.5mm§=2.2mm±0.3mm |
|
Internal pip diameter and thickness |
Φ=37±0.8mm§=1.4mm±0.2mm Φ=47±1.0mm§=1.6mm±0.2mm Φ=58±1.0mm§=1.8mm±0.2mm |
|
Pipe length |
950mm 1500mm 1600mm 1700mm 1800mm 1900mm 2000mm 2100mm |
|
Absorptive coating property |
Structure |
Cu/SS-ALN(H)/SS-ALN(L)/ALN |
Sediment method |
3 target magnetron sputtering plating |
|
Specific absorption |
As =0.93~0.96 (AM1.5) |
|
Emission ratio |
εh =0.04~0.06 (80±5) |
|
Vacuum tightness |
P≤5.0×10-3Pa |
|
Idle sunning property parameters |
Y=260~300 m2.C/KW |
|
Solar irradiation for obtaining a preset water temperature |
H≤4.7MJ/m2(Φ58) |
H=3.7~4.2 MJ/m2 |
H≤3.7MJ/m2(Φ47) |
H=2.9~3.2 MJ/m2 |
|
Average heat loss coefficient |
ULT=0.4~0.6W/(m2.) |
Structure |
All-glass double-tube co-axial structure |
|
Glass material |
High borosilicate 3.3 glass |
|
External pip diameter and thickness |
Φ=47±1.0mm§=1.6mm±0.2mm Φ=58±1.0mm§=1.8mm±0.2mm Φ=70±1.5mm§=2.2mm±0.3mm |
|
Internal pip diameter and thickness |
Φ=37±0.8mm§=1.4mm±0.2mm Φ=47±1.0mm§=1.6mm±0.2mm Φ=58±1.0mm§=1.8mm±0.2mm |
|
Pipe length |
950mm 1500mm 1600mm 1700mm 1800mm 1900mm 2000mm 2100mm |
|
Absorptive coating property |
Structure |
Cu/SS-ALN(H)/SS-ALN(L)/ALN |
Sediment method |
3 target magnetron sputtering plating |
|
Specific absorption |
As =0.93~0.96 (AM1.5) |
|
Emission ratio |
εh =0.04~0.06 (80±5) |
|
Vacuum tightness |
P≤5.0×10-3Pa |
|
Idle sunning property parameters |
Y=260~300 m2.C/KW |
|
Solar irradiation for obtaining a preset water temperature |
H≤4.7MJ/m2(Φ58) |
H=3.7~4.2 MJ/m2 |
H≤3.7MJ/m2(Φ47) |
H=2.9~3.2 MJ/m2 |
|
Average heat loss coefficient |
ULT=0.4~0.6W/(m2.) |