| Model: | JD-C011 |
|---|---|
| Brand: | JIADE |
| Origin: | Made In China |
| Category: | Metallurgy , Mining & Energy / Metallurgy & Mining / Non-metallic Mineral Deposit |
| Label: | Clay ceramsite , Volcanic ceramsite |
| Price: |
US $112
/ ton
|
| Min. Order: | 10 ton |
| Live Chat: |  | Last Online:26 Jun, 2012 |
Porcelain granule media is formed into the shape of ball by mixing with powdered superior kaolin and bauxite and pore-forming agent and granulating agent either by humidification or drying and baking and other technology. The surface of media is hard with many mini-pore inside and large specific area and is used for single layer or multi-layer filter.
Clay ceramsite
|
Composition |
SiO2 |
ALO3 |
Fe2O3 |
CaO |
MgO |
KO2+Na2O |
|
Content % |
59.88 |
16.23 |
7.84 |
3.26 |
2.04 |
3.22 |
|
Shape |
Globular |
|||||
|
Grain size |
0.5-32mm |
|||||
|
Bulk density |
1.0-1.9g/cm3 |
|||||
|
Density |
2.26g/cm3 |
|||||
|
Porosity |
55% |
|||||
|
Wear rate |
1.62% |
|||||
|
Muriatic acid soluble rate |
2.83% |
|||||
|
Sodium hydroxide soluble rate |
1.5% |
|||||
Volcanic ceramsite
|
Performance index |
Unit |
Test |
Performance index |
Unit |
Test |
|
Unit weight |
Kg/cm3 |
740 |
Surface area |
M2/g |
13.6-25.5 |
|
Specific gravity |
1:1.29 |
Compression strength |
Mpa |
5.78 |
|
|
moisture |
% |
0.9-1.0 |
Shear strength |
Mpa |
3.98 |
|
Porosity |
% |
73-82 |
Wear rate |
% |
＜1 |
|
Organics remove |
% |
≥80 |
Forming time |
hour |
27 |
|
CDO remove |
% |
≥85 |
Muriatic acid soluble rate |
% |
＜1 |
|
BDO remove |
% |
75-93 |
Exsolution material |
Trace mineral |
|
|
NH3,N remove |
% |
≥85 |
Shape |
Globular |
|