Product Description： Cementitious capillary crystalline waterproofing coating is a grey mealy coating, with chemical active composition added and ordinary portland cement based. Its action principle is mainly replies on porosity, under the action of water, chemical active composition can infiltrate into the surface then reacts to insoluble crystal, such as ettringite. The chemical active composition can boost hydration of cement, forming a large number of crystals to fill the void. Then the water can’t permeate into the cement to meet waterproofing objectives. Cementitious capillary crystalline waterproofing material has a good cementing property, a good workability on smooth reference plane, burr reference plane, outside reference plane, inside reference plane, dry reference plane, wet reference plane or water control reference plane.   Main features:
it is a green and environmental protection with long-term waterproof, corrosion-resistant anti-aging and steel protection. Have ability to permeate 2^nd times and self-repair. Easy and quick to apply, non-pollution. 1)  Non toxic and tasteless, no contamination to environment. 2)  Can be applied by brushing or spraying on concrete surface when mixing with water; dry powder can also be applied to moist or green concrete. 3)  Permanent; waterproofing resistance remain intact even after surface damage. 4)  Able to self-cure fine cracks. 5)  Easy to apply. Scope of application:  It can widely use in tunnel, dam, reservoir, power plant, nuclear power plant, cooling tower, viaduct, bridge, runway., pile foundation, wastewater treatment facility, civil engineering and other concrete construction waterproofing.     Product Specification:

Type	Cementitious Capillary Crystalline
Material	Amine and Isocyanate
Thickness	TBA
Density	Kg/sqm while thickenss is1mm.
Usage	basements, Building Coating, Road Marking Paint, Rubber Coating, Other
Application Method	Brush
Packing	Plastic Barrel, Pallet
Loading in Container	TBA
Colors	Customized
Enclosure	NONE

    Technical Standard：  

No	Item				National Standard Ⅰ		National Standard Ⅱ
1	Stability		Qualified
2	Setting Time	Initial Setting min≥		20
		Final setting h≤		24
3	Bending Resistance Mpa≥	7		2.8
		28d		3.5
4	Compressive strength, Mpa≥	7		12
		28d		18
5	Bonding strength in moistbase/ Mpa ≥			1.0
6	Seepage pressure (28d), Mpa ≥			0.8		1.2
7	Second Seepage pressure(56d),Mpa≥			0.6			0.8
8	Seepage pressure ratio(28d),%			200			500