Model: | XL-3320 |
---|---|
Brand: | XUELAI SILICONE |
Origin: | Made In China |
Category: | Chemicals / High Polymers |
Label: | Shoe Mould Making Si , Silicone Rubber , Tin-cured Silicone |
Price: |
US $6
/ KG
|
Min. Order: | 200 KG |
Live Chat: | Last Online:17 May, 2013 |
Model
|
XL-3310
|
XL-3320
|
XL-3330
|
XL-3340
|
Appearance
|
white
/translucent
|
white
/translucent
|
white
/translucent
|
white
/translucent
|
Viscosity(cps250C)
|
10000
|
15000-17000
|
26000-28000
|
20000-22000
|
Hardness (shore A)
|
10
|
20
|
30
|
40
|
Tensile Strength(MPa)
|
≥1.3
|
≥1.6
|
≥2.5
|
≥1.2
|
Tear Strength(KN/m)
|
≥12
|
≥15
|
≥23
|
≥12
|
Elongation Break (%)
|
≥300
|
≥330
|
≥350
|
≥280
|
Mix Ratio (%)
|
2%-4%
|
2%-4%
|
2%-4%
|
2%-4%
|
Retractility (%)
|
<0.3
|
<0.3
|
<0.3
|
<0.3
|
Density ( g/cm3 )
|
1.08
|
1.08
|
1.08
|
1.08
|
Pot Life(min)
|
20-40
|
20-40
|
20-40
|
20-40
|
Cured Time (hour)
|
2-5
|
2-5
|
2-5
|
2-5
|
Note: A.FAST CURE AGENT 1020 CURING IN 2 HOURS.
B.NORMAL CURE AGENT 2040 CURING IN 6 HOURS.
|
Payment Terms: | TT |
---|---|