Model: | APPEXL-NF |
---|---|
Brand: | APPEXL |
Origin: | Made In China |
Category: | Packaging , Printing & Paper / Packaging Materials / Plastic Packaging Materials |
Label: | BOPA Film , Nylon Film , lamination film |
Price: |
US $3560
/ MT
|
Min. Order: | 2 MT |
Live Chat: | Last Online:29 May, 2022 |
Professional producer for BOPA film. High product performance.
20 days delivery of a 40ft container!
BOPA films have magnificent qualities of anti-pull and anti-puncture, flexibility, strike endurance, anti-wear, flavor or smell separation, transparency, luster and printability, and wide range of temperature choices, etc.
BOPA films are especially suitable for packing of foods that deteriorate easily, frozen and cooked foods, vegetables, aquatic products and medical machines, electronic products, etc.
GUIDANCE TO TRANSPORTATION AND STORAGE:
1. Load carefully and light, avoid to be crashed and prevent from rain and strong sunshine when being transported
2. Stored in clean and dry places
3. Well piled up, avoid to be distorted or damaged by crushing
4. Keep 2 meters away from heating objects at least
5. Better to be applied within 6 months after departure from factory
THICKNESS (μm) | 12μm | 15μm | 20μm | 25μm | METHOD BY | |
DENSITY (g/cm³) | 1.15g/cm³ | ASTM D1505 | ||||
WIDTH (mm) | 300mm---2200mm | |||||
LENGTH (m) | 7500m/15000m | 6000m/12000m | 4500m/9000m | 3500m/7000m | ||
PAPER CORE | 76mm (3") or 152mm (6") | |||||
TENSILE STRENGTH (Mpa) | MD | 220 | 230 | 240 | 250 | ASTM D882 |
TD | 230 | 240 | 250 | 260 | ||
ELONGATION (%) | MD | ≤110 | ASTM D882 | |||
TD | ≤80 | |||||
THERMAL SHRINKAGE (%) | MD | 1.2 - 2.0 | ASTM D1204 | |||
TD | 0.6 - 1.2 | |||||
CORONA TREATMENT (Dyne/m) | ≥56 | ASTM D2578 | ||||
HAZE (%) | ≤2.0 | ASTM D1003 | ||||
VAPOUR TRANSMISSION (g/m²/24h) | ≤260 | ≤240 | ≤220 | ≤200 | ASTM E96 | |
OXYGEN TRANSMISSION | < 45 | <30 | <25 | <20 | ASTM D1434 | |
TRANSPARENCY (%) | 88 - 90 | ASTM D1746 | ||||
APPLICATION TEMPERATURE | -60C - 150C (-140F - 302F) | ASTM D759 |
Payment Terms: | TT/LC |
---|---|