Model: | - |
---|---|
Brand: | - |
Origin: | Made In China |
Category: | Chemicals / Organic Chemical Materials / Organic Intermediate |
Label: | - |
Price: |
-
|
Min. Order: | - |
Live Chat: | Last Online:05 Jan, 2010 |
TYPE\
SPECIFICATION |
SODIUM
|
VISCOSITY
(2% SO LUTION25 oC) mpa.s |
PH VALUE
|
CHLORIDE
(Cl-%) |
MOISTURE
(%) |
IRON
(%) |
ARSENIC
(%) |
HEAVY
METALS (Pb%) |
AVR
|
QEL PARTICLE
(number /cm2) |
MOULDS/
YEASTS (cfu/g) |
FH9
|
9.0-9.5
|
800-1000
1000-1200 |
6.5-8.0
|
<=1.8
|
<=8.0
|
<=0.03
|
<=0.0002
|
<=0.0002
|
.>=0.82
|
<=10
|
<=100
|
FM9
|
9.0-9.5
|
400-600
600-800 |
6.5-8.0
|
<=1.8
|
<=10.0
|
<=0.03
|
<=0.0002
|
<=0.0002
|
>=0.82
|
<=10
|
<=100
|
FVH9
|
9.0-9.5
|
>=1200
|
6.5-8.0
|
<=1.8
|
<=10.0
|
<=0.03
|
<=0.0002
|
<=0.0002
|
>=0.82
|
-
|
<=100
|
FH6
|
6.5-8.5
|
800-1000
1000-1200 |
6.5-8.0
|
<=1.8
|
<=10.0
|
<=0.03
|
<=0.0002
|
<=0.0002
|
-
|
-
|
<=100
|
FM6
|
6.5-8.5
|
400-600
600-800 |
6.5-8.0
|
<=1.8
|
<=10.0
|
<=0.03
|
<=0.0002
|
<=0.0002
|
-
|
-
|
<=100
|
FVH6
|
6.5-8.5
|
>=1200
|
6.5-8.0
|
<=1.8
|
<=10.0
|
<=0.03
|
<=0.0002
|
<=0.0002
|
-
|
-
|
<=100
|
TYPE\
SPECIFI-CATIONS |
DEGREE OF SUBS-TITUTE
(D.S) |
GLYCEROL LIQUOR
VISCOSITY mpa.s (2) |
VISCOSITY
(2% OLUTION, 25oC) mpa.s (1) |
PH VALUE
|
CHLORIDE
(NaCl%) |
MOISTURE
(%) |
SVA
(%) |
MOULDS/
YEASTS (cfu/g) |
HEAVY
METALS (Pb%) |
ARSENIC (%)
|
IRON (%)
|
||
FREE
|
24 HOURS
|
||||||||||||
IH10
|
IH10-1
|
>=1.00
|
950-1200
|
-
|
-
|
6.5-8.0
|
<=3.0
|
<=7.0
|
>=100
|
<=100
|
<=0.002
|
<=0.0005
|
<=0.03
|
IH10-2
|
>=1.00
|
950-1200
|
7500-10500
|
12000-16000
|
6.5-8.0
|
<=3.0
|
<=7.0
|
>=100
|
<=100
|
<=0.002
|
<=0.0005
|
<=0.03
|
|
IH9
|
>=0.92
|
950-1200
|
-
|
-
|
6.5-8.0
|
<=3.0
|
<=7.0
|
>=95
|
<=100
|
<=0.002
|
<=0.0005
|
<=0.03
|
Specification\type
|
XD-1
|
XD-2
|
XD-3
|
XD-4
|
Viscosity (2% solution, 25oC) mpa.s
|
5-40
|
5-40
|
50-100
|
100-300
|
Purity (%)>=
|
55
|
60
|
65
|
65
|
Degree of ether
|
0.50-0.70
|
0.50-0.70
|
0.60-0.80
|
0.60-0.80
|
Ph VALUE
|
8.0-11.0
|
8.0-11.0
|
7.0-9.0
|
7.0-9.0
|
Moisture (%<=
|
10.0
|
10.0
|
10.0
|
10.0
|