Refractory material for ceramics,glass,porcelain,chemical industry,
Product Description
Alumina hollow castable material
SL-1.3 SL-1.6
AL2O3 % ≥95 ≥95
Fe2O3 % ≤0.8 ≤0.8
bulk density g/cm3 ≤1.3 ≤1.6
cold compressive strength Mps ≥5 ≥8
highest service tempreture ℃ >1600 >1600
Zinc bath preproduced composed brick
AL2O3 % Bulk densty
g/cm3 Mpa cold
Compressive
strength refractoriness
℃ chang of Curve
after fire
1400℃×24h %
mullite ≥55 ≥2.4 110℃×24h
≥30 ≥1700 ±0.5
Carborndun,zirconium,silicon-aluminum seres mortar
AL2O3% ZrO2% Cr2O3% grain size
mm refractoriness remarks
Silimanite ≥60 0~0.5 ≥1790 Brickwork sillimanite
Mullite mortar ≥68 0~0.5 ≥1790 Brickwork mullite brick
Corundum mortar ≥90 0~0.5 ≥1790 Brickwork mullite corundum brick
Cement of zirconium mortar ≥65 0~0.5 ≥1790
Cement of aluminumchromium-1 ≥75 ≥3 0~0.5 ≥1790 Brickwork chromium corundum
Cement of aluminumchromium-2 ≥90 ≥5 0~0.5 ≥1790 Brickwork chromium corundum
Cement of carborundum Sic%
≥65 0~0.5 ≥1790 Brickwork carborundum and compound
Cement of chromium,zirconium,and ramming material,castable material
AL2O3% ZrO2% Cr2O3% Bulk
density
g/cm3 refractoriness
℃ Mpa cold compressive strength Moisture water
Cement of chromium corundum ramming material ≥85 ≥8 ≥3.0 ≥1790 110℃×24h
≥35 3~5
Cement of chromium corundum castable material ≥85 ≥8 ≥3.0 ≥1790 110℃×24h
≥45 5~7
Cement of zirconium corundum ramming material ≥45 ≥30 ≥3.0 ≥1790 110℃×24h
≥35 3~5
Cement of zirconium corundum castable material ≥45 ≥30 ≥3.0 ≥1790 110℃×24h
≥45 3~7
Silicon-aluminum,zirconium-aluminum products series
AL2O3% Fe2O3% Apparent ponosity
% Bukl density
g/cm3 MPa Cold compressive strength initial softing point under load
Combined antistripping high alumina brick phosphate ≥75 ≤1.2 ≤22 ≥2.55 ≥60 ≥1550
Silicon line stone brick ≥65 ≤0.5 ≤18 ≥2.45 ≥60 ≥1600
Mullite brick ≥70 ≤0.5 ≤18 ≥2.55 ≥70 ≥1650
Corundum-mullite brick ≥80 ≤0.5 ≤18 ≥2.65 ≥80 ≥1650
Agglutination corundum brick 90 ≥90 ≤0.5 ≤18 ≥3.0 ≥90 ≥1700
Agglutination corundum brick 95 ≥95 ≤0.5 ≤18 ≥3.0 ≥90 ≥1700
Zirconium corundum brick ≥60 ZrO2
≥20 ≤22 ≥3.0 ≥75 ≥1600
Chromium corundum brick ≥90 Cr2O3
≥4 ≤20 ≥3.0 ≥75 ≥1600
purpose Widely used in high temperature kiln-furnace as metallurgy, chemical industry,electron,glass and so on
Corborundum and compound product
SiC % AL2O3% Apparent rate
% Bulk density
g/cm3 Initial softening point under load Cold compressive strength
MPa
Carbonrundum product ≥75 - ≤21 ≥2.40 ≥1520 ≥70
Mullite combined with silicon product ≥60 ≥8 ≤20 ≥2.40 ≥1520 ≥80
Corundum silicon carbide product ≥60 ≥30 ≤20 ≥2.50 ≥1530 ≥90
High aluminum silicon carbide product ≥30 ≥40 ≤22 ≥2.45 ≥1500 ≥50
Carbon sillimanite brick product ≥30 ≥45 ≤22 ≥2.50 ≥1500 ≥60
Cellular corundum carbonrundum slideway ≥10 ≥80 ≤22 ≥2.90 ≥1600 ≥85
Silicon nitride combined with carborundum brick ≥72 Si3N4≥15 ≤17 ≥2.60 ≥1550 ≥100
purpose Used for color metallurgy,porcelain and ceramics industry,cement rotary kiln mouth,and high temperature of glass annealing ovean and all kinds of furnace
Send Inquiry to this Member
This member assumes full responsibility for the content of this listing. DIYTrade accepts no responsibility whatsoever in respect of such content.
To report fraudulent or illegal content, please
click here.
China Suppliers Quick Searching:
,