HIPS Granules / High Impact Polystyrene
Specification:
| Property | Unit | Test Method | Test Condition | HIPS |
| Tensile Strength | kg/cm2
( MPa) |
ASTM D-638
( ISO527) |
23°C | 220
(22) |
| Tensile Elongation | % | ASTM D-638
( ISO527) |
23°C | 40 |
| Flexural Strength | kg/cm2
( MPa) |
ASTM D-790
( ISO178) |
23°C | 440
(43) |
| Flexural Modulus | kg/cm2*104
( MPa) |
ASTM D-790
( ISO178) |
23°C | 2.3
(2260) |
| Izod
Impact Strength |
kg-cm/cm
( J/m ) |
ASTM D-256
( ISO R180 ) |
23°C
1/4'' bar |
11.0
(108) |
| Vicat Softening
Temperature |
°C | ASTM D-1525
(ISO306B) |
Annealed
80°C×2Hr 1/8'' bar |
95 |
| Heat Deflection
Temperature |
°C | ASTM D-648
( 75/A) |
Annealed
80°C×2Hr 1/8'' bar |
88 |
| Melt
Flow Index |
g/10 min | ASTM D-1238
( ISO1133 ) |
200°C×5Kg
( 49N ) |
5.5 |
| Residual Monomer | ppm max. | - | - | 700 |
| Molding
Shrinkage |
% | FCFC
Method |
23°C | 0.4~0.6 |
| Specific Gravity | - | ASTM D-792
( ISO1183 ) |
23°C/23°C | 1.04 |
| Flammability | - | UL-94 | FILE NO.
E162823 |
1/16" HB
NC |
HIPS-688
| Raw materials description | |||||||
| Standard | Injection molding grade | Colour | White | ||||
| Application | High impact, high heat-resisting, low temperature resistance,good regidity,according with food hygienic standard, be widely used in toy and home appliances manufacture. | ||||||
| Remark | High impact, high heat-resisting, extrusion molding. | ||||||
| Raw materials technique data | |||||||
| Property items | Test condition | Method | Test result | Units | |||
| Basic performance | Melt flow rate | 200°C/5kg | ISO 1133 | 4.6 | g/10min | ||
| Density | ISO 1183 | 1.04 | g/cm3 | ||||
| Water absorption | ISO 62 | <0.1 | % | ||||
| Physical property | Process contractibility rate | ISO 294 | 0.4-0.7 | % | |||
| Mechanical behavior | Stretch yield stress | 23°C | ISO 527 | 23 | Mpa | ||
| Percentage elongation | 23°C | ISO 527 | 45 | % | |||
| flexural strengh | 23°C | ISO 178 | 46 | Mpa | |||
| Flexural modulus | 23°C | ISO 178 | 2260 | Mpa | |||
| Izod impact | 23°C | ISO 180 | 115 | j/m | |||
| Rockwell hardness | 23°C | ASTMD-785 | 65 | L | |||
Thermal property |
Vicat softening point | B10/oil | ISO 306 | 95 | °C | ||
| distortion temperature(non-anneal) | 1.82Mpa | ISO 75-2 | 79 | °C | |||
| Other propery | Fire resistance | UL 94 | HB | ||||
| residual monomer | <400 | ppm max | |||||