| Category: | Metallurgy , Mining & Energy / Metallurgy & Mining / Bars, Rods, Angles, and Stainless Steel Shapes |
| Label: | High Performance , Incoloy 800H , UNS N08810 |
| Price: |
-
|
| Min. Order: | - |
| Live Chat: |  | Last Online:27 Aug, 2019 |
*Similar Grade
|
GB |
Trademark |
UNS |
DIN EN/DIN |
W-Nr. |
BS EN/BS |
|
NS1102 NS112 |
Incoloy 800H Incoloy 800HT |
N08810 N08811 |
X10NiCrAlTi32-20 |
1.4876 |
NA15H |
*Product Forms
Pipe, Tube, Sheet, Strip, Plate, Round Bar, Flat Bar, Forgings, Hexagon, Wire
*Brief
Nickel-iron-chromium alloys having the same basic composition as INCOLOY alloy 800 but with significantly higher creep-rupture strength. The higher strength results from close control of the carbon, aluminum, and titanium contents in conjunction with a high-temperature anneal. Used in chemical and petrochemical processing, in power plants for super-heater and reheater tubing, in industrial furnaces, and for heat-treating equipment.
*Chemical Composition,%
|
Alloy |
% |
Ni |
Fe |
Cr |
C |
Mn |
Si |
P |
S |
Al+Ti |
Ti |
|
800H |
Min |
30.0 |
39.5 |
19.0 |
0.05 |
|
|
|
|
0.30 |
0.15 |
|
Max |
35.0 |
|
23.0 |
0.10 |
3.0 |
0.10 |
0.03 |
0.02 |
1.20 |
0.60 |
|
|
800HT |
Min |
30.0 |
39.5 |
19.0 |
0.06 |
|
|
|
|
0.30 |
0.25 |
|
Max |
35.0 |
|
23.0 |
0.10 |
3.0 |
0.10 |
0.03 |
0.02 |
1.20 |
0.60 |
*Typical Physical & Mechanical Property(Annealed)
|
Density |
Melting point |
Tensile strength, MPa |
Yield strength, MPa |
Elongation,% |
|
8.0 g/cm3 |
1357-1385℃ |
≥550 |
≥240 |
≥25 |
*Specification
|
Rod, Bar, Wire, Forgings |
ASTM B408/ASME SB408, ASTM B564/ASME SB564, ISO 9723/9724/9725 |
|
Plate, Sheet, Strip |
ASTM A240/A480/B409/B906/ASME SA240/SA480/SB409/SB906, ISO 6208 |
|
Pipe, Tube |
ASTM B163/ASME SB163, ASTM B407/B829/ASME SB407/SB829, ASTM B514/B775/ASME SB514/SB775, ASTM B515/B751/ASME SB515/SB751, ISO 6207 |
|
Others |
ASTM B366/ASME SB366(Fittings) |
*Feature
Incoloy 800H and 800HT are both austenitic high-strength solid-solution nickel-iron-chromium alloy with controlled levels of carbon, aluminium, titanium, silicon and manganese and controlled content of (Al + Ti). The analyses are similar to that of Incoloy 800,but a special solution anneal treatment (with grain sizes ≥ 90 μm/ASTM No. 4) gives significantly increased creep-rupture strength for Incoloy 800H above 600 ℃ and highest creep-rupture strength for Incoloy 800HT above 700 ℃ due to the precipitation of TiC.
*Application
Steam/hydrocarbon reforming for components such as: transfer piping, catalyst tubes (in low pressure processes) and quench-system piping,
Cracking tubes used in the production of acetic anhydride and ketene – high strength, resistance to carburization and to dry hydrogen chloride and chlorine