Die Cut Original 3M™ High Performance Double Coated Tape 9088-200 and 9088F-200
Product Description
3MTM Double Coated Tapes with 3M Modified Acrylic Adhesive 375 provides an excellent balance of adhesive peel and shear performance. The adhesive system used on this product provides good adhesion to both high and low surface energy substrates. The initial tack provided ensures that a bond of good integrity is achieved soon after application.
Double Coated Acrylic Tape 9088-200 and 9088F-200
9088-200 9088F-200
Value-priced, durable, general purpose tapes have a wide service temperature range from -10ºF (-23ºC) to 300ºF (148ºC) as well as:
High peel and shear strength
High initial tack
Excellent UV resistance
Chemical resistance – including plasticizers used in many plastic materials
Excellent transparency – leaves no visible bond lines, making it great for laminating
Adhesive lays down flat for a smoother surface
Ideal for many low and high surface energy bonding applications
Uses a solventless adhesive coating process that is good for the environment and application performance
With both the paper and film liner, you can take on almost any project
Bond most any substrate with a single product – from glass, metal and powder coated paint to most common plastics.
Works on both LSE and HSE surfaces.
Easy to cut, resistant to tearing and available in a variety of sizes.
Replace mechanical fasteners – like screws, bolts and rivets in many applications.
Solvent-free formula.
Low odor.
Available in level wound rolls.
3M™ High Performance Double Coated Tape 9088F200 with a film liner has the same attributes of the paper liner as well as:
No debris – “clean”.
Crisp die-cutting – especially rotary.
Fast processing with small pieces.
Useful for laser registration – color dependent.
Improved visibility and transparency.
Details
Suitable for a broad range of applications.
Excellent for applications requiring high adhesion and high transparency.
0.5 mil PET carrier is excellent for graphic displays.
Adhesive 375 bonds to nearly any surface, rough or smooth.
Resists UV, chemicals and high temperatures for long-term bond.
3M™ High Performance Double Coated Tape 9088-200 features a modified acrylic adhesive that bonds to most substrates, including difficult-to-stick-to substrates. This adhesive is applied on both sides of a .5 mil PET carrier which adds strength and stability and is excellent for a wide range of applications. A glassine paper liner makes for efficient conversion processing.
3M™ Adhesive 375 Family Provides High Initial Tack
3M™ High Performance Double Coated Tape 9088-200 features our 3M™ Adhesive 375, formulated for very high initial adhesion and excellent peel and shear performance. This high-performance adhesive has been tested for high peel and shear performance on substrates including stainless steel, polycarbonate, glass, HDPE, ABS and high pressure laminate.
A Remarkable Combination of Strength and Sustainability
Like many of our double sided tapes, 3M™ High Performance Double Coated Tape 9088-200 is designed as a go-to industrial tape for long term adhesion in a very broad range of applications where a thicker tape is desired. The adhesive is applied at 3.7 mils to each side of a strong, highly transparent .5 mil polyester (PET) film carrier. The tape resists UV, chemicals, solvents and high temperatures. A 3 mil glassine paper liner adds dimensional stability for effective and efficient die-cutting and other conversion methods.
Construction:
product | 3M Double Coated Tape 9088-200 | 3M Double Coated Tape 9088F-200 |
Tape (Total W/O Liner) Thickness | 7.9 mils / 0.20mm | 7.9 mils / 0.20mm |
Adhesive1 Thickness |
Acrylic 3.7mils / 0.094mm | Acrylic 3.7 mils / 0.094mm |
Carrier Type Thickness | PET 0.5 mils / 0.012mm | PET 0.5 mils / 0.012mm |
Adhesive2 Thickness | Acrylic 3.7 mils / 0.094mm | Acrylic 3.7 mils / 0.064mm |
Liner Type | 58# Glassine(94g/m²) 3.2 mils / 0.08mm | Red Polypropylene Film 3.2 mils / 0.08mm |
Liner Color | Printed Red 3M | Solic red |
Color | Clear | Clear |
Adhesive | Solventless Modified Acrylic | Solventless Modified Acrylic |
Temperature Range
Short Term / Long Term |
148°C (300°F) / 90°C (194°F) | 148°C (300°F) / 90°C (194°F) |
Substrate Compatability | ABS, PET, PVC, Foil, Glass, Metal, Paper, Plastic, Polystyrene,
Polypropylene, Polycarbonate, Powder Coated Paint |
|
Liner Color | Printed Red 3M(the picture below) | Solic red (the picture below) |
Note: Adhesive 1 is on the interior of the roll, exposed when unwound, Adhesive 2 is on the exterior of the roll, exposed when liner is removed. The thickness listed is based on a calculation from manufacturing controlled adhesive coat weights using a density of 1.012 g/cc. While past data pages have listed nominal thicknesses, the coat weight (and theoretical caliper) has not changed.
Typical Physical Properties and Performance Characteristics
I. 180 Peel Adhesion: ASTM D-3330 (Modified: 2 mil aluminum foil backer)
Substrate | 72 hr Dwell @ RT |
Stainless Steel | 159 oz/in 174 N/100 mm |
Polycarbonate | 166 oz/in 182 N/100 mm |
Glass | 153 oz/in 167 N/100 mm |
ABS | 135 oz/in 148 N/100 mm |
HDPE | 55 oz/in 60 N/100 mm |
II. Static Shear Strength
Temperature | Size | Weight | Minutes |
72⁰ (23⁰C) 50%RH | 1” x 1” | 1000 grams | 10,000 |
158⁰F (70⁰C) 50% RH | 1” x 1” | 500 grams | 10,000 |
*Test terminated at 10,000 minutes
Environmental Performance
UV Resistance – When properly applied, nameplates and decorative trim parts are not adversely affected by outdoor exposure.
Bond Build-up: The bond strength of 3M™ Adhesive 375 increases as a function of time and temperature.
Temperature/Heat Resistance: Adhesive 375 is usable for short periods (minutes, hours) at temperatures up to 300⁰F (150⁰C) and for intermittent longer periods (days, weeks) up to 195⁰F (90⁰C).
Lower Temperature Service Limit: --10⁰F (-23⁰C).
Markets:
Transportation
Appliance
Automotive
Construction
Signage
Electronics
General Industrial
Application Ideas:
Point of Purchase Displays
Indoor/Outdoor Signage
Paper Bonding and Packaging
Splicing
Mounting of Plastic Parts
Mounting of Furniture and Decorative Trims
Recommended Applications
POP/POS displays Self-adhesive mounting of furniture trim
Sealing profiles and cable ducts Fabric and leather stitching
Blind manufacturers Print finishing
Splicing Light Boxes
Indoor/Outdoor Signs Paper Bonding and Packaging
Metal Fabrication Splicing and Bonding Sports Equipment Home Decoration
Mounting of Plastic Parts Mounting in Electronics
Mounting in Furniture