1 Introduction
Composed of 80%Fe, 20%Sic and B type metal elements. With high permeability, low loss and good stability, it can meet modern electronic product's requirements in high frequency, large current, small size and energy saving, and also can replace silicon steel, permalloy and ferrite in electricity utility and electronic products.
2 Application
Widely used for distribution transformer core, medium frequency transformer core, inverter core, high switch power supply, pulse transformer core, magnetic amplifier core, saturable reactor core, PFC inductor core, filter inductor core and so on.
3 Feature
High saturation flux density--to reduce winding turns, minimize product size
High resistivity, low coercivity--to improve production performance
Low loss(1/3 to 1/5 of silicon sheet)--to cool temperature, improve efficiency
Low excitation--decrease no-load current, and noise
Adjustable permeability--adopt different heat treatment process according to different requirement
High temperature stability--long-term operation under 130° C
4 Property
Model : 1K101
|
Performance Index |
Rate |
Performance Index |
Rate |
|
Saturation flux density Bs (T) |
1.56 |
Saturation magnetostriction λs |
27*10^-6 |
|
Curie temperature Tc(℃) |
410 |
Density d(g/cm^3) |
7.18 |
|
Crystallization Tx(℃) |
535 |
Resistivity ρ(Ωm²/m) |
130 |
|
Hardness HV Kg/mm^2 |
960 |
Coercivity Hc(A/m) |
<4 |
5 Specification
|
Item |
Width (mm) |
Thickness (μm) |
Thickness deviation (μm) |
Lamination factor |
|
spray strip1K101
|
100-220 |
25 |
±2 |
>0.86 |
|
shear strip1K101
|
2-220 |
25 |
±2 |
>0.86 |
Note: Normal width: 120,140,70,213mm, the specifications can be customized.
6 Comparison
Zhongyue versus Hitachi
|
1K101 |
|
Bs/T |
Br/T |
Hc/(A/m) |
Ss/(W/kg) |
Ps/(VA/kg) |
|
Zhongyue |
Before annealing |
1.08 |
0.8 |
3.91 |
1.33 |
0.45 |
|
Hitachi |
1.01 |
0.75 |
5.76 |
2.4 |
0.32 |
|
|
Zhongyue |
After annealing
|
1.56 |
1.21 |
2.09 |
0.2 |
0.15 |
|
Hitachi |
1.56 |
1.13 |
1.93 |
0.072 |
0.11 |
Before annealing After Annealing
red : Hitachi black: zhongyue
7 Model
|
Code |
Width(mm) |
Thickness(μm) |
|
J1K101030282 |
30 |
28 |
|
J1K101035282 |
35 |
28 |
|
J1K101045282 |
45 |
28 |
|
J1K101050282 |
50 |
28 |
|
J1K101060282 |
60 |
28 |
|
J1K101065282 |
65 |
28 |
|
J1K101100282 |
100 |
28 |
|
J1K101150282 |
150 |
28 |
|
J1K101200282 |
200 |
28 |
Code J 1K101 30 28 2
Instruction shear material width(with 1decimal) thickness deviation