Model: | TZRS-VT200 (2X) |
---|---|
Brand: | Volsun |
Origin: | Made In China |
Category: | Electronics & Electricity / Insulation Material |
Label: | heat shrink tubing , viton shrink tubing , viton shrink tube |
Price: |
US $0.18
/ pc
|
Min. Order: | 200 pc |
Last Online:11 Dec, 2015 |
TZRS-VT200(2X) modified fluoroelastomer heat-shrinkable tubing is highly abrasion and cut-through resistant and can withstand a wide variety of fuels, lubricants, acids and highly corrosive fluids at temperatures up to 200°C. In addition to its high continuous operating temperature and chemical-resistance properties, this tubing is very flexible and is easily marked by hot-stamp or printwheel methods. When heated in excess of 175°C (347°F), TZRS-VT200(2X) tubing rapidly shrinks to a skintight fit. TZRS-VT200(2X) tubing is rated for continuous operation from –55°C (–67°F) to 200°C (392°F).135°C/275°F.
Cross-linked fluoroelastomer
Property |
Test Method |
Test Method |
Tensile strength |
≥12MPa |
ASTM D 638 |
Ultimate elongation |
≥400% |
ASTM D 638 |
Tensile strength Ultimate elongation |
≥300% |
250℃×168h |
Flammability |
Self-quenching In 15 seconds |
ASTM D 2671 |
Longitudinal expansion rate |
-5%~+5% |
ASTM D 2671 |
Heat shock |
No cracking |
300℃×4h |
Breakdown strength |
≥12kV/mm |
ASTM D 2671 |
volume resistivity |
≥109Ω.cm |
ASTM D 876 |
Size(mm) |
As Supplied (mm) D |
After Recovery (mm) |
Standard Length
|
|
Inner diameter d |
Wall thickness w |
(m/spool) |
||
Φ2.4 |
≥2.4 |
≤1.2 |
0.51±0.08 |
200 |
Φ3.2 |
≥3.2 |
≤1.6 |
0.76±0.13 |
100 |
Φ4.8 |
≥4.8 |
≤2.4 |
0.89±0.18 |
50 |
Φ6.4 |
≥6.4 |
≤3.2 |
0.89±0.18 |
50 |
Φ9.5 |
≥9.5 |
≤4.8 |
0.89±0.18 |
50 |
Φ12.7 |
≥12.7 |
≤6.4 |
0.89±0.18 |
50 |
Φ19.1 |
≥19.1 |
≤9.5 |
1.07±0.21 |
30 |
Φ25.4 |
≥25.4 |
≤12.7 |
1.25±0.30 |
30 |
Φ38.1 |
≥38.1 |
≤19.1 |
1.40±0.38 |
30 |
Φ50.8 |
≥50.8 |
≤25.4 |
1.65±0.43 |
30 |