VG-201 Fiberglass Sleeving Coated With PVC Resin
This kind of fiberglass sleeving is the non-alkali fiberglass braided sleeving coated with polyvinyl chloride resin. It is produced with the process of therm- plasticization.
The polyvinyl chloride fiberglass sleeving possesses good qualities of dielectric, chemical resistance, excellent softness and elasticity. It can be used for wiring insulation and mechanical protection for electrical machinery, electric appliances, electrical instruments and apparatus, medical instruments and apparatus, wireless sets, TV sets and domestic electrical appliances of electrical fans, washing machine etc.
Length: 1000+20-10mm
(Continuous length may be negotiated.)
|
Bore diameter |
Wall Thickness |
||
|
Nominal |
Tolerance |
Minimum |
Maximum |
|
0.5;0.8 |
±0.10 |
0.20 |
0.50 |
|
1;1.5 |
±0.15 |
0.20 |
0.75 |
|
2;2.5 |
±0.20 |
0.20 |
0.75 |
|
3; |
±0.25 |
0.20 |
0.75 |
|
4;5;6; |
±0.25 |
0.30 |
0.75 |
|
7;8 |
±0.50 |
0.30 |
0.90 |
|
9;10;12;14;16;18;20;23;25;27 |
±0.50 |
0.40 |
0.90 |
Property Requirements
|
Property |
Requirements |
||
|
Resistance to soldering heat |
Pass (only for sleeving having nominal bore diameter up to and including 5mm) |
||
|
Bending after heating |
No Cracking or detachment of coating shall be visible after bending around mandrels after 96h at 1300c |
||
|
Bending at low temperature |
No Cracking of detachment of coating shall be visible after bending around mandrels while at -250c |
||
|
BreakdownVoltage,kv,min.
|
Room Temp. |
Elevated temp. |
Damp heat |
|
Central value |
4.0 |
1.2 |
1.2 |
|
Lowest individual value |
2.5 |
0.8 |
0.8 |
|
Insulation resistance MΩ |
At room temperature:103
|
||
|
Flame propagation method A ,sec., max. |
60,in addition, the indicator flag on any one of the three test specimens shall not be burned nor shall have flaming or glowing particles or flaming drops ignite the cotton |
||
|
Temperature index |
105 |
||
|
Bore Diameter |
Wall Thickness |
||
|
Nominal |
Tolerance |
Nominal |
Tolerance |
|
1;1;5 |
+0.20
|
0.30 |
±0.10 |
|
2;2.5 |
+0.30
|
0.30 |
±0.10 |
|
3;3.5 |
+0.30
|
0.50 |
±0.15 |
|
4;5;6 |
+0.40
|
0.50 |
±0.15 |
|
7;8;9 |
+0.50
|
0.50 |
±0.15 |