Model: | 001 |
---|---|
Brand: | suinaxin |
Origin: | Made In China |
Category: | Chemicals / Plastic Materials |
Label: | PP , Polypropylene , PE |
Price: |
-
|
Min. Order: | - |
Live Chat: | Last Online:09 Jun, 2015 |
Properties |
ASTM |
Test Condition |
Unit |
Typical Values |
|
|
|
|
|
J001M |
J002W |
Density |
D-792 |
- |
g/cm3 |
1.20 |
1.07 |
Moistureabsorption |
D-570 |
23 C,24hrs |
% |
0.03 |
0.03 |
Melt fiow rate |
D-1238 |
230 C/2.16k |
g/10min |
9 |
9 |
Tensile Strength |
D-638 |
10mm/min |
MPa |
26 |
24 |
Strain at break |
D-638 |
10mm/min |
% |
15 |
30 |
Flexural strength |
D-790 |
2mm/min |
MPa |
40 |
40 |
Flexural modulus |
D-790 |
2mm/min |
MPa |
1980 |
1960 |
|
D-256 |
3.2mm,23 C |
KJ/ m2 |
4.2 |
4.5 |
IZOD Impact Strength(notched) |
|
3.2mm,-40 C |
KJ/ m2 |
- |
- |
Rockwell Hardness |
D-785 |
R-Scale |
- |
95 |
93 |
HDT |
D-648 |
1.82MPa |
C |
70 |
70 |
Coefficient of linear thermal expansion |
D-696 |
- |
*10-5/ C |
10 |
10 |
Volume Resistivity |
D-257 |
- |
OHM·m |
1017 |
1017 |
Resist electric arc track sex |
D-495 |
- |
sec |
- |
- |
Dielectric strength Insulation |
D-149 |
- |
Mv/m |
43 |
43 |
Mold Shrinkage |
D-955 |
1mm |
% |
0.6~1.1 |
0.6~1.1 |
23,,60RH Dissipation factor |
D-150 |
1MHz |
- |
- |
- |
Flammability |
UL-94 |
1/16" |
- |
V-0 |
V-0
|