Introduction

1. It is a good filter media for depth filtration because of three dimensional fiber structures

2. It is made from different diameters stainless steel fibers

3. It is sintered in a high temperature vacuum furnace

4. It is filter efficiency is high because of differential fiber layers density gradients

5. High dirt holding capacity

6. Easy to be fabricated, pleated and welded

7. Corrosion resistance

Technical Data

LEERSF5: 5 Micron, 6600 Pa, 47 (L/Min*Dm2), 75%, 5 Mg/Cm2, 0.30 ± 10% MM, 32 ± 20% Mpa

LEERSF7: 7 Micron, 5000 Pa, 63 (L/Min*Dm2), 76%, 6 Mg/Cm2, 0.30 ± 10% MM, 36 ± 20% Mpa

LEERSF10: 10 Micron, 3700 Pa, 105 (L/Min*Dm2), 77%, 6 Mg/Cm2, 0.37 ± 10% MM, 32 ± 20% Mpa

LEERSF15: 15 Micron, 2450 Pa, 140 (L/Min*Dm2), 79%, 7 Mg/Cm2, 0.40 ± 10% MM, 23 ± 20% Mpa

LEERSF20: 20 Micron, 2000 Pa, 280 (L/Min*Dm2), 80%, 13 Mg/Cm2, 0.48 ± 10% MM, 23 ± 20% Mpa

LEERSF25: 25 Micron, 1500 Pa, 360 (L/Min*Dm2), 78%, 19 Mg/Cm2, 0.62 ± 10% MM,20 ± 20% Mpa

LEERSF30: 30 Micron, 1230 Pa, 520 (L/Min*Dm2), 79%, 24 Mg/Cm2, 0.63 ± 10% MM,23 ± 20% Mpa

LEERSF40: 40 Micron, 960 Pa, 670 (L/Min*Dm2), 79%, 34 Mg/Cm2, 0.68 ± 10% MM, 26 ± 20% Mpa

LEERSF60: 60 Micron, 650 Pa, 1300 (L/Min*Dm2), 85%, 36 Mg/Cm2, 0.68 ± 10% MM, 25 ± 20% Mpa

Raw Material

SS 316L

Working Temperature

-200 - 600 Degree Celsius

Number of layers:

1. One layer (Sintered Metal Fiber Felt)

2. Two layers (One Side Protective Wire Mesh /Sintered Metal Fiber Felt)

3. Three layers (One Side Protective Wire Mesh /Sintered Metal Fiber Felt/One Side Protective Wire Mesh)

Regular Size:

500mm*500mm, 500mm*1000mm, 1000mm*1000mm (other sizes can be customized according to the clients requirements)