| Model: | - |
|---|---|
| Brand: | HTKD |
| Origin: | Made In China |
| Category: | Construction & Decoration / Shaped Building Material |
| Label: | aluminum tube , T6 , High Strength |
| Price: |
-
|
| Min. Order: | 1 ton |
| Live Chat: | Last Online:20 May, 2015 |
Detailed Product Description
| Surface: | Mill Finish, Anodized And Colored | Tensile Strength: | 524Mpa |
| Elongation: | 11% | E⁄Gpa: | 71 |
| Temper: | T6 | Alloy: | 1000|2000 |
High Strength T6 Aluminium Tube White With Abrasion Resistance
1) Alloy: 1000,2000,5000,6000,7000 series .
2) Temper: T6
3) Specification: accoring clients request or drawing .
4) Surface: mill finish, anodized and colored etc.
5)color: white, yellow, red, purple ,blue, black, Camouflage ,assorted colors etc
6) Delivery time: approx 20-30 days after confirming order.
6) Minimum order quantity: several kgs per size
7) The term of payment: T/T,LC
8) Packing: Export standard, wooden box packing or according clients request .
9).Feature: high strength aluminium alloy,
10)Supply ability:1000ton/month
7001/7075 etc aluminum pipe production technology
1.Aluminum bar through the peeling after punch 1200 t extruder extrusion forming Ø and x 2.0
2.Large diameter through the cold machine after cold drawn, with fire degradation process to the necessary
3.specifications, is commonly Ø 8.5 x 0.72 ~ Ø 7.9 x 0.72 MM
4.Aluminum tube forming later, straightening machine straightening, cutting machine cut to size
5.Chamfering process, is the place where the cut hair cut into smooth
6.Surface oxidation color for the core assembly, cut loose fire
7.Assembly product
7075 aluminum is a cold treatment forging alloy, high strength, and far better than mild steel.
7075 aluminum tube is one of the most powerful alloy in business. Common corrosion resistance,good
mechanical capacity and anodic reaction. Fine grain can make the deep drilling performance even better, tool
abrasion resistance increase, and thread rolling is more different.
7075 aluminum chemical component
| Alloy, chemical composition, mechanical properties | |||||||||||||
| chemical composition(The mass fraction)% | |||||||||||||
| Grade | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Zr | Remark | Al | |
| 7075 | 0.40 | 0.50 | 1.2-2.0 | 0.30 | 2.1-2.9 | 0.18-0.28 | - | 5.1-6.1 | 0.20 | - | single 0.05 | total 0.15 | the rest |
| Mechanical properties | |||||||||||||
| state | Thickness | Tensile strength Rm/Mpa | Extension strength Rp0.2/Mpa | Elongation/% | |||||||||
| A | A50mm | ||||||||||||
| ≮ | |||||||||||||
| T6 | ≤25 | 530 | 460 | 6 | 4 | ||||||||
| T6510 T6511 | ＞25-60 | 540 | 470 | 6 | - | ||||||||
| T73 T73510 T73511 | ≤25 | 485 | 420 | 7 | 5 | ||||||||
| T76 | ≤6 | 510 | 440 | - | 5 | ||||||||
| T76510 T76511 | ＞6-50 | 515 | 450 | 6 | 5 | ||||||||
7075 aluminum tube processing features
7075 aluminum is called a super-high strength aluminum alloy, the yield strength of alloy is close to tensile
strength. Yield strength and intensity is relatively high .But low plasticity and high-temperature strength,it
shouldbe used for bearing structure at room temperature and below 120℃.The alloy is easy to be processed,
havingbetter corrosion resistance and higher toughness. It is widely used in aviation and aerospace field, and
become one of the most important structural materials in this field.
physical property and mechanical capacity
1.tensile strength:524Mpa
2.0.2% yield strength 455Mpa
3.elongation: 11%
4.elasticity modulus:E⁄Gpa:71
7075 aluminum tube product feature
1.high strength and heat-treatable alloy.
2. good mechanical capacity
3. good workability
4. easy processing, good abrasion resistance.
5. good corrosion resistance and oxidation resistance.