| Model: | E308L-16 |
|---|---|
| Brand: | TEMO |
| Origin: | Made In China |
| Category: | Metallurgy , Mining & Energy / Metallurgy & Mining / Bars, Rods, Angles, and Stainless Steel Shapes |
| Label: | welding wire , welding electrode , welding rod |
| Price: |
US $1500
/ Ton
|
| Min. Order: | 0.2 Ton |
| Live Chat: | Last Online:26 Jul, 2014 |
| Item NO. | GB/TB | AWS | ||||||
| WEA002 | E308L-16 | E308L-16 | ||||||
| Description：
Type of Cr19Ni10Mo ultra-low carbon stainless steel with coating of titanium calcium electrode.The carbon content in deposited metal less than or equal to 0.04％ with good intergranular corrosion satisfying.Both AC/DC connection applicable with excellent welding performance. |
||||||||
| Application:
WEA002 Stainless Steel Electrode apply to welding of stainless-steel of low carbon(Cr19Ni10).Can also be used to weld of corrosion resistance stainless steel under the operation temperature lower than 300℃.It is mainly used in synthetic fiber, fertilizer, petroleum equipment. |
||||||||
| Chemical composition of Deposited metal(％): | ||||||||
| C | Mn | Si | Cr | Ni | Mo | Cu | S | P |
| ≤0.04 | 0.5-2.5 | ≤0.90 | 18.0-21.0 | 9.0-11.0 | ≤0.75 | ≤0.75 | ≤0.030 | ≤0.040 |
| Mechanical Performance of deposited Metal: | ||||||||
| Rm(Mpa) | A(％) | |||||||
| ≥520 | ≥35 | |||||||
| ※The deposited metal corrosion resistance test and titanium content determined by supply and demand both sides negotiation. | ||||||||
| Reference Current:(DC﹢or AC) | ||||||||
| Diameter (mm) | Φ2.0 | Φ2.5 | Φ3.2 | Φ4.0 | ||||
| Current (A) | 25-50 | 50-80 | 80-110 | 110-160 | ||||
| Notes:(Ⅰ)Please bake WEA002 Stainless Steel Electrode for 1 hour at 150℃ before welding .(Ⅱ)We s est you to do the welding by DC and control the current to avoid redenning problem of rodes. By AC, the depth will not be enough. | ||||||||
right:.��slPM�cy border-left:none;width:108pt'>Φ4.0 Φ5.0 Current (A) 60-90 90-120 140-180 170-230 Notes:(Ⅰ)Please bake WE557 Low Alloy Steel Electrode for 1 hour at about 380℃ before welding .(Ⅱ)Clean the surface to be welded thoroughly to remove surface contaminations.(Ⅲ)Short arc must be used when welding and the weld joint shoulds not be too wide.