| Model: | lldpe |
|---|---|
| Brand: | KL |
| Origin: | Made In China |
| Category: | Chemicals / Plastic Materials |
| Label: | lldpe , reccyled ldpe , ldpe film grade |
| Price: |
US $800
/ mt
|
| Min. Order: | 20 mt |
| Live Chat: | Last Online:15 May, 2014 |
1.LLDPE recycled film grade for packaging film
2.Free sample,lowest price
3.film/injection/moulding
4.CIQ SGS BV
1, LLDPE film grade
|
Tests |
Value |
Unit |
|
Melt Flow Rate (MFR) |
2.0±0.4 |
g/10min |
|
Density |
920±2 |
Kg/cm3 |
|
Tensile Strengthat Yield |
8 |
Mpa ≥ |
|
Tensile Strengthat Break |
12 |
Mpa ≥ |
|
haze |
15 |
%≤ |
|
Packing |
In 25 kg PP woven bags,20MT/20’FCL |
|
2, LLDPE for Master Batch Use
|
Tests |
Value |
Unit |
|
Melt Flow Rate (MFR) |
20 |
g/10min |
|
Density |
0.924 |
g/cm3 |
|
Tensile Strength |
MD12 |
Mpa |
|
TD 10 |
||
|
Elongation at Yield |
13 |
% |
|
Elongation at Break |
200 |
|
|
Dark Drop Impact |
105 |
g |
|
Brittle Temperature(F 50) |
-70 |
°C |
|
Vicat Softening Point |
90 |
°C |
|
Packing |
In 25 kg PP woven bags,20MT/20’FCL |
|
3, LLDPE Powder Rotational Molding Grade for Tank Use
|
Tests |
Value |
Unit |
|
Melt Flow Rate (MFR) |
3.2 |
g/10min |
|
Density |
0.939 |
g/cm3 |
|
Melting Point |
127 |
°C |
|
Tensile Yield Strength |
21 |
Mpa |
|
Tensile Strength at Break |
28 |
Mpa |
|
Elongation at Break |
1,100 |
% |
|
Flexural Modulus |
750 |
Mpa |
|
Brittle Temperature |
<-60 |
°C |
Application: Make barrela, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating
Storage: Shelf life: It should avoid damp, contaminated and direct sun light during transport.And should be stored in ventilated and dry place. Do not put it with flammable and corrosive substances together,and away from the fire.