HY- E series addition molding silicone is generally named two-components silicone

rubber, Part A and part B. It features an exceptional fluidity and good operability. 

The mixing ratio is 1:1 (10:1),mainly be suitable for making molds application.

Typical Applications

HY- E series addition molding silicone could be mainly used for making concrete

stones, wax molds, PU molds, resin molds, gypsum casting, candle molding and

chocolate , candy and any other FDA food product mold making,prototyping etc.

HY-E620 Silicone Rubber is has been used for years to make tire pattern molds .

Characteristics 

1.Low shrinkage (less than 0.1% )

2.High tensile and tear strength with high copy times 

3.Easy for operation (mixing ratio at 1:1 /10:1)

4.Very good flow and easy for pouring operation

5.Fast and non-shrink cure at room temperature which can be accelerated considerably by the application of heat

Operation instruction of HY-E Series molding silicone:

1. Pls clear the model and tool totally before operation to prevent cure inhibition.

2.Weigh the two part correctly by electronic weight in two separate container .

3. Mixing the two part in 1:1/10:1 and stir part A and part B evenly in 2-3 minutes .

4.And get the mixture for vacuum-pumping for de-air the bubble in around 2-3

minutes . (If there is no vacuum machine, pls pour the mixture carefully and slowly

down the side of the mold frame so that less bubbles caused)

5. Enclose the product (the original model) with four plastic plates or wooden plates.

6. Clean your products and brush a layer of release agent(detergent or soap water) on

your product.

7. Pour the vacuumed mixture into the model frame from the side of the mold frame .

Notice : 

As our E-series silicone is platinum cure silicone , which is very easy to cause

cure inhibition , so pls do remember thoroughly clean the model and tool before

operation . Besides , pls avoid the liquid E-series silicone contact or mix with the

following material , otherwise the silicone won’t be cured :

1. Liquid condensation silicone ( condensation silicone not completely cured or organic

tin compounds )

2 .Sulphur, sulfide and sulfur rubber materials.

3. Amine compounds as well as contains the amine materials.

4 .Pewter solder flux.

SHELF LIFE: 

8-10 months when stored under 24℃ in original unopened packages.

PACKAGE: 

If ratio is 1:1 :Packed in 20kg/pail + 20kg/pail and 200kg/pail + 200kg/pail.

If ratio is 10:1 :Packed in 20kg/pail + 2kg/pail and 200kg/pail + 20kg/pail.

For more information, pls feel free to contact Susan

Tel: +86-0755-8931148

Mob: +86-18938867567

Skype & Email: hys (at) resinpu (dot) com