Home > Products > Construction & Decoration > Heat Insulation

Operating temperature

Depends on the material conditions of use,heat source variety and environment condition,etc.

Manufacturing technique

All kinds of Aluminum silicate swinging fiber blankets,made by swinging fiber forming process of ordinary type, standard type, high pure type,high aluminum type, HAZ Ceramic type,HZ Ceramic type cotton as fiber raw material, by away of needling, heat setting, vertical & horizontal cutting and curly process ,etc.

Different density and thickness of fiber blanket, provide to users a wide range of material selection, in order to obtain the best heat insulation structure and energy efficiency.

Aluminum silicate swinging fiber blankets’diameter are uniformity,fiber is length,with Low content of slag ball,make the fibers’extent of interweave,resistance to delamination,performance, weather-proof,flexibility and tensile strength an overall improvement,thus improve the application performance of blankets, reduce the material wastage.

Aluminum silicate swinging fiber blankets are don’t use any binder, ensure that the product has good reliability and stability in various environment.

 

 

 

 

Technical 

 

  

 

function

 

 

 

 

 

 

 

 

 

Low thermal conductivity, low thermal capacity

 

 

 

 

 

 

 

 

 

 

 

 

 

Excellent thermal stability and thermal shock resistance

 

 

 

 

 

  

 

 

Good tensile strength

 

  

 

 

 

 

Excellent heat insulation ,

 

fireproofing,sound-absorbing

 

 

  

 

Application

 

 

 

 

 

 

 

 

 

Industrial building materials furnace, heating device, heat  

 

 

 

 

pipeline wall lining.

Electricity boiler,steam turbine and nuclear electricity heat insulation.

Chemical industrial high temperature reaction equipment and heating equipment insulation lining.

High-rise building fireproof & heat insulation

Kiln door & lid 

 

 

 

heat 

 

  

 

insulation

 

 

 

 

 

 

 

 

 

High temperature 

 

 

 

 

filter material filtration material

Item		COM	ST	HP	HA	HAZ	HZ
Classification Temperature ℃		1100	1260	1260	1360	1360	1430
Operating Temperature ℃		＜1000	1050	1100	1200	1200	1350
Volume densitykg/m3		96 128	96 128	96 128	128 160	128 160	128 160
Heat conductivity coefficient（w/n.k）volume density128kg/m3		-4（1000℃）	-3（1000℃）	-3（1100℃）	-3（1250℃）	-3（1250℃）	-3（1250℃）
Permanent linear contractive（%） (holding temperature for 24h，volume density128kg/m3)		0.09（400℃） 0.176（800℃）	0.09（400℃） 0.176（800℃）	0.09（400℃） 0.176（800℃） 0.22（1000℃）	0.132（600℃） 0.22（1000℃）	0.132（600℃） 0.22（1000℃）	0.76（600℃） 0.22（1000℃）
Tensile strength MPa（volume density128kg/m3）		0.08-0.12	0.08-0.12	0.08-0.12	0.08-0.12	0.08-0.12	0.08-0.12
Chemical composition (%)	AL2O3	42-44	45-46	47-49	52-55	45-46	39-40
	AL2O3+SIO2	96	97	99	99	---	---
	AL2O3+SIO2+ZrO2