Model: | ER316L ER309L |
---|---|
Brand: | tianshen |
Origin: | Made In China |
Category: | Electronics & Electricity / Electronics Stocks |
Label: | ER316L , welding wire , stainless steel wire |
Price: |
US $4000
/ ton
|
Min. Order: | 1 ton |
Live Chat: | Last Online:16 Jan, 2013 |
Stainless steel solid core wires can be used inert gas shielded welding, MIG welding (TIG).
Stainless steel solid core wires can be used inert gas shielded welding, MIG welding (TIG). Also can be used for submerged arc welding. Stainless steel MIG welding can reach high-effective welding, and easy to implement welding automation, widely used in surfacing and thin connect, etc.
Standard: AWS/A5.20 E70T-1 GB/T 10045 E500T-1 |
|
|
|
|
|
|
USE FOR |
(Compostion) |
Mechanics ability |
Package |
Dia of spool |
Size(mm) |
|
ER308L |
18Cr- Mainly for welding 18Cr-8Ni steel; |
C:0.064% ; Mn:1.65%; Si:0.42% ;Ni:8.33%;Cr:17.10% |
Mpa 1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 ; TIG:1.0-4.5 |
ER304L |
17Cr-8Ni;Mainly for welding 17Cr-8Ni steel; |
C:0.028% ;Mn:1.65%;Si:0.42%;Ni:8.33% Cr:17.10% |
Mpa 1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 ; TIG:1.0-4.5 |
ER308 |
19Cr-9 |
C:0.064%;Mn:1.65% |
Mpa 1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 |
Mainly for welding 19Cr-9Ni steel; |
Si:0.42%;Ni:10.33% Cr:20.10% |
TIG:1.0-4.5 |
||||
ER308L |
20Cr-9Ni |
C:0.024%;Mn:1.65% |
Mpa 1200 |
5/12.5/15/20 |
100/270/300 |
MIG:0.8-1.6 |
Mainly for welding 20Cr-9Ni steel; |
Si:0.42%;Ni:10.33% Cr:20.10% |
TIG:1.0-4.5 |
||||
ER309 |
20Cr-13Ni |
C:0.064%;Mn:1.65% |
Mpa 1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 |
Mainly for welding 20Cr-3Ni steel; |
Si:0.42%;Ni:14.33% Cr:20.10% |
TIG:1.0-4.5 |
||||
ER309L |
20Cr-14Ni |
C:0.024%;Mn:1.65% |
Mpa 1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 |
Mainly for welding 20Cr-14Ni steel |
Si:0.42%;Ni:14.33% Cr:20.10% |
TIG:1.0-4.5 |
||||
ER309Lsi |
20Cr-14Ni |
C:0.024%;Mn:1.65% |
Mpa1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 |
Mainly for welding 20Cr-4Ni steel |
Si:1.02%;Ni:14.33% Cr:20.10% |
TIG:1.0-4.5 |
||||
ER321 |
16Cr-7Ni |
C:0.064%;Mn:1.65% Si:0.42%; |
Mpa 1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 |
Mainly for welding 16Cr-7Ni steel |
Ni:8.33% Cr:17.10% Ti:0.73% |
TIG:1.0-4.5 |
||||
ER347 |
16Cr-9Ni |
C:0.064%;Mn:1.65% Si:0.42%; |
Mpa 1200 |
5/10/15/20 |
100/270/300 0 |
MIG:0.8-1.6 |
Mainly for welding 16Cr-9Ni steel |
Ni:9.33% Cr:17.10% |
TIG:1.0-4.5 |
||||
|
(Ta+Nb(10*C)-10 |
|